Polymers are extensively used in various industries due to their versatility, durability and cost-effectiveness. To ensure functionality and longevity, polymer parts must have sufficient strength to endure external forces without deformation or breakage. Traditional approaches to increasing part strength involve adding more material; however, balancing strength to weight relationships is challenging. This paper explorers the viability of manufacturing lightweight components using a microcellular foaming polymer. Microcellular foaming has emerged as a helpful tool to achieve an optimal strength-to-weight ratio; offering advantages such as lightweight, improved mechanical properties, reduced material usage, better insulation and improved cost-effectiveness. It can also contribute to improved fuel efficiency and reduced carbon emissions, making them environmentally favourable. The combination of additive manufacturing (AM) and microcellular foaming has opened new possibilities for design innovation. This text highlights the challenges and efforts in incorporating foaming techniques into 3D printing processes, specifically fused filament fabrication (FFF). This study reveals that microcellular polymers are a viable option when balancing part strength and weight. The experiments completed during the formulation of this paper demonstrated that lightweight LW-PLA parts were significantly lighter than standard PLA parts and that a design of experiments approach can be used to optimise strength properties and provide insights into optimising manufacturability. Microcellular polymers present an opportunity for lighter and stronger 3D printed parts, offering potential energy and material savings for sustainable manufacturing practices.

This paper presents an experimental study of a novel automated manufacturing process that integrates cold embossing to add complex features, such as micro-Fresnel lens designs, onto a 3D-printed ABS polymer component. The research demonstrates that precise control over process parameters, including embossing time (E_t) and velocity (E_v), is critical for successful feature replication. Gloss analysis confirmed that surface softening as a crucial prerequisite for embossing was successfully achieved using a vapour smoothing (VS) chamber that was developed and optimised for the process. High-speed automation using a 6-axis KUKA robot allowed 48 embosses to be completed in just over one minute, highlighting its efficiency over conventional hot embossing (HE) methods. Results showed that an E_t (0.01 s) prevented feature replication as there was insufficient time to allow for polymer flow, while an optimal E_t (0.1 s) produced high-quality embosses across all test segments. Additionally, this study identified that while insufficient cycle times hinder polymer flow, extended durations can lead to surface hardening, prohibiting replication. These findings pave the way for integrating Diffractive Optical Elements into 3D-printed parts, potentially enhancing precision, functionality, and productivity beyond the capabilities of standard 3D-printing processes.