To comprehensively understand the impact of various environmental factors on the self-healing process of graphene-modified asphalt, this study employs molecular dynamics simulation methods to investigate the effects of aging degree (unaged, short-term aged, long-term aged), asphalt type (base asphalt, graphene-modified asphalt), healing temperature (20 °C, 25 °C, 30 °C), and damage degree (5 Å, 10 Å, 15 Å) on the self-healing performance of asphalt. The validity of the established asphalt molecular models was verified based on four physical quantities: density, radial distribution function analysis, glass transition temperature, and cohesive energy density. The simulated healing time for the asphalt crack model was set to 200 ps. The following conclusions were drawn based on the changes in density, mean square displacement, and diffusion coefficient during the simulated healing process under different influencing factors: Dehydrogenation and oxidation of asphalt molecules during the aging process hinder molecular migration within the asphalt crack model, resulting in poorer self-healing performance. As the service life increases, the decline in the healing performance of graphene-modified asphalt is slower than that of base asphalt, indicating that graphene-modified asphalt has stronger anti-aging properties. When the vacuum layer in the asphalt crack model is small, the changes in the diffusion coefficient are less pronounced. As the crack width increases, the influence of various factors on the diffusion coefficient of the asphalt crack model becomes more significant. When the crack width is large, the self-healing effect of asphalt is more dependent on these influencing factors. Damage degree and oxidative aging have a more significant impact on the healing ability of graphene-modified asphalt than healing temperature.

A high-performance composite modifier ER-SBS-T was prepared through the mixing of epoxy resin with a fast-melting styrene–butadiene–styrene modifier (SBS-T) to enhance material properties. This study evaluated the fatigue characteristics of ER-SBS-T-modified asphalt using a linear amplitude sweep test, and 70# base asphalt, SBS-modified asphalt, and SBS-T-modified asphalt were used as control groups. The fatigue life of ER-SBS-T-modified asphalt was determined according to viscoelastic continuous damage (VECD) theory. The findings indicated that as the ER-SBS-T modifier content increased, both the maximum value and the cumulative damage limit value increased, while the rate of change of decreased. At strain levels of 2.5% and 1%, the fatigue life of the modified asphalt improved with increasing ER-SBS-T content. However, at a strain level of 5%, the modified asphalt exhibited no significant trend in fatigue life across different ER-SBS-T contents. ER-SBS-T-modified asphalt with a modifier content of >10% demonstrated favorable fatigue performance suitable for practical engineering applications.

To overcome the limitations of conventional high-viscosity high-elasticity modified asphalt, including high production costs, phase separation, and thermal degradation, this study introduces a novel fast melting Styrene-Butadiene-Styrene modifier (SBS-T) for asphalt modification. The primary novelty of SBS-T lies in its ability to mitigate phase separation and thermal degradation while simplifying the production process, thereby offering a more robust and cost-effective alternative. The viscoelastic properties of SBS-T-modified asphalt were characterized through frequency sweep tests under varying loading conditions, while its fatigue behavior was quantitatively assessed using the Simplified Viscoelastic Continuum Damage (S-VECD) model. The results indicate that the SBS-T-modified asphalt exhibits outstanding viscoelastic performance across a broad range of temperatures and loading frequencies, and can better adapt to the temperature and load changes in complex pavement environments. Among them, the influence of long-term aging on the linear viscoelastic characteristics of SBS-T-modified asphalt is greater than that of ultraviolet aging. The SBS-T-modified asphalt also shows better stiffness and resistance to shear deformation. The fatigue life of asphalt gradually decreases with the deepening of the aging degree, among which the impact of long-term aging on fatigue life is greater than that of ultraviolet aging. Under different aging conditions, SBS-T-modified asphalt has shown good fatigue performance and is suitable for practical engineering applications.