This study was undertaken to evaluate the potential of demolished building waste (DBW) as aggregates in alkali-activated concrete (AAC). A recent road-widening activity led to the demolition of commercial buildings along National Highway 275, Bangalore-Bantwal, India. DBW was collected from these sites and processed manually at the laboratory facility of CHRIST (Deemed to be University). Processing of DBW was done to obtain both waste coarse and fine aggregates from demolished concrete and brick waste units, respectively. AAC was synthesized by fly ash, ground granulated blast furnace slag, sodium hydroxide, sodium silicate, along with waste aggregate replacement rates of 0, 25, 50, and 75% by weight of natural aggregates. Fresh and hardened properties of developed concrete mixtures were experimentally determined. Results of the study indicate that 28-day compressive strength of 30.4 and 21 MPa was obtained for AAC with 25 and 50% DBW aggregates, which was 8.6 and 36.9% lower than control mix, respectively. Further, there was an increase in the water absorption and a reduction to acid resistance for all the AAC mixes with DBW aggregates. Based on the results obtained, it was observed that AAC with 25 and 50% DBW aggregates find great potential in civil engineering applications.

With the advent of the COVID-19 pandemic, the global consumption of single-use surgical masks has risen immensely, and it is expected to grow in the coming years. Simultaneously, the disposal of surgical masks in the environment has caused plastic pollution, and therefore, it is exigent to find innovative ways to handle this problem. In this study, surgical masks were processed in a laboratory using the mechanical grinding method to obtain recycled surgical masks (RSM). The RSM was added in doses of 0%, 1%, 2%, 3%, and 4% by volume of geopolymer bricks, which were synthesized with ground granulated blast furnace slag (GGBS), rice husk ash (RHA), sand, and sodium silicate (Na₂SiO₃) at ambient conditions for a duration of 28 days. The developed bricks were tested for compressive strength, flexural strength, density, water absorption, efflorescence, and drying shrinkage. The results of the study reveal that compressive strength and flexural strength improved with the inclusion of RSM in the bricks. The highest values of compressive strength and flexural strength were 5.97 MPa and 1.62 MPa for bricks with 4% RSM, respectively. Further, a reduction in the self-weight of the bricks was noticed with an increase in RSM. There was no pronounced effect of RSM on the water absorption and efflorescence properties. However, the RSM played a role in reducing the drying shrinkage of the bricks. The sustainability analysis divulges the catalytic role of RSM in improving material performance, thereby proving to be a potential candidate for low-carbon material in the construction industry.

Masonry-infilled reinforced concrete (MI-RC) frames are widely used in building construction due to their enhanced stiffness and load-carrying capacity under lateral loads. However, their seismic performance is often governed by failure mechanisms such as diagonal cracking, crushing, and frame–infill separation. This study investigates the effectiveness of geogrid surface reinforcement in improving the strength of masonry prisms through experimental investigations. Further, the influence of geogrid surface reinforcement on the seismic response of MI-RC frames is studied numerically. Experimental investigations were conducted to determine the mechanical properties of constituent materials, including clay bricks, cement mortar, and brick masonry prisms with and without geogrid reinforcement. The results indicate that geogrid confinement enhances the compressive strength of masonry prisms by 16.67%, while also reducing crack propagation and improving stress distribution characteristics. The experimentally obtained nonlinear stress–strain properties were incorporated into numerical models developed in OpenSees, where masonry infill panels were represented using equivalent diagonal strut elements. In-plane nonlinear static pushover analysis was performed on three models: a bare RC frame, an RC frame with unreinforced masonry infill, and an RC frame with geogrid-reinforced masonry infill. The results demonstrate that the inclusion of masonry infill significantly increases the lateral load capacity and stiffness of RC frames, while geogrid reinforcement further enhances structural performance. Specifically, geogrid-reinforced infill improved lateral load capacity by 8.2%, initial stiffness by 59.2%, and ductility by 48% compared to unreinforced infill systems. This study highlights that geogrid surface reinforcement provides an efficient strengthening technique for masonry infill systems, leading to improved strength, stiffness, ductility, and energy dissipation characteristics, particularly in the early deformation phase. Moreover, the comparison of damage using the expended energy-based damage index confirms the benefit of using geogrid surface reinforcement in controlling the progression of damage during lateral deformation. The findings contribute to a better understanding of the seismic response of masonry-infilled RC frames and support the adoption of geosynthetic-based retrofitting strategies for enhanced structural safety.