Even today, breast cancer remains a global public problem, with a high mortality rate among women. Nanoparticle (NP) based systems are developed to enhance drug delivery, reducing the toxic effect of medicine molecules. By using iron oxide nanoparticles for cancer treatment, several advantages were highlighted: the ability to target specific locations derived from their magnetic properties and reduced side effects. The aim of this study was to examine on breast cancer cell line the anticancer potential of γ-Fe₂O₃ NPs loaded with doxorubicin (DOX) and stabilized with carboxymethylcellulose sodium (CMCNa). The γ-Fe₂O₃ NPs were synthesized by laser pyrolysis technique and their nanometric size and crystallinity were confirmed by X-ray diffraction and transmission electron microscopy. The loading efficiency was estimated by using absorption and fluorescence spectroscopy. The DOX conjugated//CMCNa coated γ-Fe₂O₃ NPs proved through the biological studies to have a good anticancer effect through the inhibition of tumoral cell proliferation, disruption of the cellular membrane, induction of cell death and reduced effects on normal breast cells. Our data showed that DOX cytotoxicity increases significantly when conjugated with ɣ-Fe₂O₃ and ɣ-Fe₂O₃_CMCNa, a 50% reduction of cancer cell viability was obtained with a concentration around 0.1 µg/mL.

The purpose of this study was to investigate the effectiveness in photodynamic therapy of iron oxide nanoparticles (γ-Fe₂O₃ NPs), synthesized by laser pyrolysis technique, functionalized with 5,10,15,20-(Tetra-4-sulfonatophenyl) porphyrin tetraammonium (TPPS) on human cutaneous melanoma cells, after only 1 min blue light exposure. The efficiency of porphyrin loading on the iron oxide nanocarriers was estimated by using absorption and FTIR spectroscopy. The singlet oxygen yield was determined via transient characteristics of singlet oxygen phosphorescence at 1270 nm both for porphyrin functionalized nanoparticles and rose bengal used as standard. The irradiation was performed with a LED (405 nm, 1 mW/cm²) for 1 min after melanoma cells were treated with TPPS functionalized iron oxide nanoparticles (γ-Fe₂O₃ NPs_TPPS) and incubated for 24 h. Biological tests revealed a high anticancer effect of γ-Fe₂O₃ NPs_TPPS complexes indi-cated by the inhibition of tumor cell proliferation, reduction of cell adhesion, and induction of cell death through ROS generated by TPPS under light exposure. The biological assays were combined with the pharmacokinetic prediction of the porphyrin.

The purpose of this study was to investigate the synthesis of iron oxide nanoparticles under two different conditions, namely high and low gas flow rates, using laser pyrolysis and to examine the influence of laser power. The attained nanoparticles have been characterised regarding their stability and hydrodynamic dimensions by dispersive light scattering analysis (DLS), structure–X-ray diffraction (XRD), elemental composition–energy-dispersive X-ray spectroscopy (EDS) and X-ray photoelectron spectroscopy (XPS), and morpho-structural characterisation achieved by transmission electron microscopy (TEM) and selected-area electron diffraction (SAED). For a better understanding of the laser power influence, the residence time was also calculated.

The enhancement of seed germination by using nanoparticles (NPs) holds the potential to elicit the synthesis of more desired compounds with important biomedical applications, such as preventing protein glycation, which occurs in diabetes. Here, we used 7 nm and 100 nm ZnO and 4.5 nm and 16.7 nm Fe₂O₃ NPs to treat sunflower seeds. We evaluated the effects on germination, total phenolic content, and the anti-glycation potential of extracted polyphenols. Sunflower seeds were allowed to germinate in vitro after soaking in NP solutions of different concentrations. Polyphenols were extracted, dosed, and used in serum albumin glycation experiments. The germination speed of seeds was significantly increased by the 100 nm ZnO NPs and significantly decreased by the 4.5 nm Fe₂O₃ NPs. The total phenolic content (TPC) of seeds was influenced by the type of NP, as ZnO NPs enhanced TPC, and the size of the NPs, as smaller NPs led to improved parameters. The polyphenols extracted from seeds inhibited protein glycation, especially those extracted from seeds treated with 7 nm ZnO. The usage of NPs impacted the germination speed and total polyphenol content of sunflower seeds, highlighting the importance of NP type and size in the germination process.

The laser pyrolysis technique was used in the synthesis of magnetic iron oxide nanopowders in the presence of ethanol vapors as a sensitizer. This technique uses the energy from a continuous-wave CO₂ laser operating at a 9.25 μm wavelength, which is transferred to the reactive precursors via the excited ethanol molecules, inducing a rapid heating of the argon-entrained Fe(CO)₅ vapors in the presence of oxygen. For a parametric study, different samples were prepared by changing the percentages of sensitizer in the reactive mixture. Moreover, the raw samples were thermally treated at different temperatures and their morpho-structural and magnetic properties were investigated. The results indicated a high degree of crystallinity (mean ordered dimension) and enhanced magnetic properties when high percentages of ethanol vapors were employed. On the contrary, at low ethanol concentrations, due to a decrease in the reaction temperature, nanoparticles with a very low size were synthesized. The raw particles have a dimension in the range of 2.5 to 10 nm (XRD and TEM). Most of them exhibited superparamagnetic behavior at room temperature, with saturation magnetization values up to 60 emu/g. The crystalline phase detected in samples is mainly maghemite, with a decreased carbon presence (up to 8 at%). In addition to the expected Fe-OH on the particles surfaces, C (and O) bearing functional groups such as C-OH or C=O that act as a supplementary hydrophilic agent in water-based suspension were detected. Using the as-synthesized and thermally treated nanopowders, water suspensions without or with hydrophilic agents (CMCNa, L-Dopa, chitosan) were prepared by means of a horn ultrasonic homogenizer at 0.5 mg/mL concentrations. DLS analyzes revealed that some powder suspensions maintained stable agglomerates over time, with a mean size of 100 nm, pH values between 4.8 and 5.3, and zeta-potential values exceeding 40 mV. All tested agents greatly improved the stability of 250–450 °C thermally treated NPs, with L-Dopa and Chitosan inducing smaller hydrodynamic sizes.

The present study investigates the synthesis and dispersibility process of iron oxide nanoparticles using laser pyrolysis with isopropanol vapors as a sensitizer agent. Similar to previous experiments (iron oxide nanoparticles synthesized by laser pyrolysis using ethylene as sensitizer gas), iron pentacarbonyl (Fe(CO)₅) was employed as an iron precursor; however, instead of the classic ethylene, isopropanol was chosen as a sensitizer, which indicated beneficial features (especially enhanced dispersibility in water) in the as-synthesized nanoparticles. Structural and elemental analysis confirmed the size range of the nanoparticles (nanometric), with crystallite sizes under 10 nm. Both raw nanoparticles, as well as the oleic acid stabilized ones, exhibited excellent colloidal stability in both water and organic fluids (Toluene, Chloroform, and DMSO): around 100 nm hydrodynamic diameter and more than 40 mV for zeta potential. The study highlights the advantages of using isopropanol as a sensitizer in the production of high-purity iron oxide nanoparticles from laser pyrolysis, particles that showcase superior dispersibility and functionalization potential.