This study tackles the critical demand for sustainable synthesis methods of reduced graphene oxide (rGO), highlighting the environmental drawbacks of conventional chemical processes. We introduce a novel, green synthesis technique involving the irradiation of a 500 eV argon ion beam, which not only facilitates the creation of micro-patterned rGO on a graphene oxide (GO) film but also enables simultaneous material characterization and patterning. By adjusting the irradiation exposure time between 0 and 80 s, we achieve meticulous control over the attributes and the reduction process of the material. The use of X-ray photoelectron spectroscopy (XPS) allows for real-time monitoring of the reduction from GO to rGO, evidenced by a notable reduction in the intensities of C-O, C=O, and O-C=O bonds, and an increase in C-C bond intensities, indicating a significant reduction level. Our research demonstrates the efficient production of eco-friendly rGO using precise, controlled argon ion beam irradiation, proving its advantages over traditional methods. These results contribute to the development of sustainable material science technologies, with potential applications in electronics, energy storage, and more.

This study presents a novel method for the photocatalytic synthesis of 4-aryl-6-(3-coumarinyl) pyrimidin-2 (1H)-ones (a coumarin derivative) using strawberry dye-sensitized TiO₂ (SD-TiO₂) under visible light. The synthesis of 4-aryl-6-(3-coumarinyl) pyrimidin-2 (1H)-ones was achieved through a three-component, one-pot condensation reaction involving 3-acetyl coumarin, aldehydes, and urea, utilizing SD-TiO₂ as a reusable and innovative photocatalyst at room temperature. The resulting SD-TiO₂ photocatalyst was thoroughly characterized using FT-IR, XPS, XRD, SEM, and BET. The efficacy of SD-TiO₂ was evaluated by comparing it to pristine TiO₂ in terms of photocatalytic activity, and the optimal conditions for the synthesis process were determined. Notably, the SD-TiO₂ photocatalyst exhibited a maximum yield of the compound, reaching up to 96% in just 30 min with a catalyst concentration of 1 mg/mL. This yield surpasses traditional thermal procedures employing reflux conditions, where 1 mg/mL of SD-TiO₂ is sufficient to complete the reaction. The resulting 4-aryl-6-(3-coumarinyl) pyrimidin-2 (1H)-ones were further characterized using ¹H-NMR and ¹³C-NMR. Moreover, the stability of the SD-TiO₂ photocatalyst was confirmed through recyclability experiments and spectroscopic characterization, demonstrating its practicality for up to three consecutive reaction cycles.