Systematic studies were conducted at one of the uranium deposits in Kazakhstan. Native strains of Acidithiobacillus ferrooxidans bacteria were found in leaching solutions at the deposit. The modeling of iron species in the culturing medium was analyzed using Medusa software v.2.0.5. To intensify the process, the bacterial strains were propagated in laboratory conditions, and strains available in the laboratory were added. The ability of bacteria to oxidize divalent iron to trivalent iron at 8 °C in laboratory conditions was established, but the oxidation rate was low. It was found that the limiting stage of bioleaching use in deposit conditions is the temperature mode, the content of divalent iron, and oxygen. A biomass volume of 15 L was initially cultivated under laboratory conditions, and subsequently scaled up to 3 m³ in production using three 1 m³ pachucas with air aeration. In addition, pilot tests were carried out directly in production conditions and biomass in the volume of over 30 m³ was produced. The kinetics of the oxidation process of divalent iron to trivalent iron in 1 g/h under production conditions was established. The features of the bioleaching process at the field are shown as follows: since production, the solution contains the main microelements for the nutrition and reproduction of bacteria, and recommendations for the use of bioleaching are proposed. Research has established that under conditions of a shortage of divalent iron in the solution, sulfuric acid is formed due to sulfur-containing substances. It was observed that for the effective conversion of divalent iron to trivalent iron, bacteria of the provided strain and air (oxygen) supply are sufficient. The corresponding recommendations were issued during the work.

This study presents findings regarding the kinetics of ferrous iron oxidation in solution mediated by Acidithiobacillus ferrooxidans bacteria within a continuous-flow bioreactor employing diverse types of immobilizers. The objective is to augment the rate of ferrous iron oxidation in solutions utilizing an immobilizer for Acidithiobacillus ferrooxidans strains. Immobilization represents a promising avenue for enhancing the efficiency of Fe²⁺ oxidation via acidophilic ferrooxidizing bacteria, leading to a several-fold increase in oxidation rate. A comparative analysis was conducted to evaluate the efficacy of different types of immobilizer in facilitating iron oxidation within a continuous-flow bioreactor, including the application of wood chips coated with Fe(OH)₃. The results indicate that wood chips coated with iron hydroxide serve as effective type of immobilizer, facilitating the robust attachment of Acidithiobacillus ferrooxidans via electrostatic interactions between negatively charged bacteria and positively charged surfaces. Experimental investigations were conducted using novel immobilization matrices in pilot-scale tests simulating the underground borehole leaching (UBL) of uranium. The bioactivation of leaching solutions enhances the efficiency and environmental compatibility of UBL compared to conventional chemical oxidation methods. The relationships between redox potential and ferric iron content in bioactivated solutions during the UBL of uranium were delineated. The significance of this study lies in its elucidating the pivotal role of Fe²⁺ oxidation in uranium extraction processes, particularly in the context of UBL. By employing bioactivation mediated by Acidithiobacillus ferrooxidans, the study demonstrates not only enhanced uranium extraction efficiency, but also markedly improved environmental sustainability compared to traditional chemical oxidation methods. The findings reveal crucial correlations between redox potential and ferric iron concentration in bioactivated solutions.