Styrene (St) was used as comonomer and glycidyl methacrylate (GMA) as grafting monomer to prepare SEBS-g-(GMA-co-St) graft copolymers via melt grafting. Then, the graft copolymers were employed as a compatibilizer for melt blending polypropylene (PP) and hydrogenated styrene-butadiene-styrene (SEBS) triblock copolymers. The effects of the amount of GMA in the graft copolymers on thermal properties, rheology, crystallization, optical and mechanical properties, and microstructure of the blends were investigated. The results show that GMA and St were successfully grafted onto SEBS. The GMA amount in the graft copolymer significantly influenced the comprehensive properties of PP/SEBS/SEBS-g-(GMA-co-St) blends. The epoxy groups of GMA reacted with PP and SEBS, forming interfacial chemical bonds, thereby enhancing the compatibility between PP and SEBS to varying extents. After introducing SEBS-g-(GMA-co-St) into PP/SEBS blends, crystallinity decreased, crystal size increased while transmittance remained above 91% with rising GMA amount in the graft copolymers, indicating excellent optical properties. Notched impact strength and elongation at break of the blends showed a trend of first increasing and then decreasing with increased amounts of GMA in the graft copolymers. When the amount of GMA in the graft copolymers was 3 wt%, the blends exhibited optimal toughness with notched impact strength and elongation at break of 30,165.82 J/m² and 1445.40%, respectively. This was attributed to the tightest dispersion interface adhesion and maximum matrix plastic deformation, consistent with the mechanical performance results.

The melt-free radical grafting of glycidyl methacrylate (GMA) onto poly (lactic acid) (PLA) with styrene (St), α-methylstyrene (AMS), and epoxy resin (EP) as comonomers in a twin-screw extruder was used to prepare PLA-g-GMA graft copolymers. The prepared graft copolymers were then used as compatibilizers to prepare PLA/PPC/PLA-g-GMA blends by melt blending with PLA and polypropylene carbonate (PPC), respectively. The effects of different comonomers in the PLA-g-GMA graft copolymers on the thermal, rheological, optical, and mechanical properties and microstructure of the blends were studied. It was found that the grafting degree of PLA-g-GMA graft copolymers was increased to varying degrees after the introduction of comonomers in the PLA-g-GMA grafting reaction system. When St was used as the comonomer, the grafting degree of the PLA-g-GMA graft copolymer increased most significantly, from 0.8 to 1.6 phr. St as a comonomer also most improved the compatibility between PLA and PPC, and the haze of the blends was reduced while maintaining high transmittance. In addition, the PLA-g-GMA graft copolymer with the introduction of St as a comonomer significantly improved the impact toughness of the blends, while the thermal stability and tensile strength of the blends remained largely unchanged.