The objective of this work is to improve the mechanical properties of polylactic acid (PLA) by incorporating cellulose nanocrystals (CNC) previously obtained from a cellulose pulp extracted from olive tree pruning (OTP) waste. Composites were manufactured by melt processing and injection moulding to evaluate the effect of the introduction of CNC with conventional manufacturing methods. This OTP-cellulose pulp was subjected to a further purification process by bleaching, thus bringing the cellulose content up to 86.1%wt. This highly purified cellulose was hydrolysed with sulfuric acid to obtain CNCs with an average length of 267 nm and a degradation temperature of 300 °C. The CNCs obtained were used in different percentages (1, 3, and 5%wt.) as reinforcement in the manufacture of PLA-based composites. The effect of incorporating CNC into PLA matrix on the mechanical, water absorption, thermal, structural, and morphological properties was studied. Maximum tensile stress and Young’s modulus improved by 87 and 58%, respectively, by incorporating 3 and 5%wt. CNC. Charpy impact strength increased by 21% with 3%wt. These results were attributed to the good dispersion of CNCs in the matrix, which was corroborated by SEM images. Crystallinity index, glass transition, and melting temperatures were maintained.

The research addresses challenges in food safety related to the migration of contaminants from plastics to food. It focused on the physicochemical and sensory degradation of olive oils packaged in polyethylene terephthalate (PET) and subjected to thermal exposure at 40 °C and 60 °C for several weeks and a subsequent 12 months of storage, as well as the stability and migration of compounds from the PET packaging itself. Olive oils (OO) from Spanish supermarkets (a mixture of refined and virgin, with commercial identifications of mild and intense) were selected and subjected to thermal treatments at 40 °C and 60 °C for 1, 2, and 3 weeks, followed by 12 months of storage. The treatments were conducted through the following two independent experiments: Experiment A focused on immediate analysis post-thermal treatment, while Experiment B included a 12-month storage period post-thermal treatment. The presence of antimony (Sb) was analyzed using acid digestion with nitric acid (HNO₃) and high-resolution inductively coupled plasma mass spectrometry (HR-ICP-MS), while the metals cadmium (Cd), copper (Cu), lead (Pb), and iron (Fe) were analyzed using inductively coupled plasma mass spectrometry (ICP-MS). The PET characterization was assessed using Fourier transform infrared spectroscopy in the mid-infrared range (FT-IR/MIR), carbonyl index, and differential scanning calorimetry (DSC). The results showed increases in the acidity index by 0.29%, the peroxide value by 25.92%, and the K₂₆₈ coefficient by 51.22% between the control sample and the most severe treatments, with more pronounced effects observed after 12 months. Sensory quality declined, with reduced intensity of the “fruity” attribute and increased presence of the “rancid” defect. PET degradation was reflected in an increase in the carbonyl index and greater structural amorphization. Fe was the predominant metal, and Sb concentration increased after thermal treatments. The lack of studies on the raw consumption of oils packaged in PET and the concerns about the migration of compounds from the packaging to the food highlight the relevance of this research. This study provides new insights into the effects of thermal exposure and storage on the migration of PET contaminants into oils, contributing to the development of strategies to ensure food safety and product quality.

Globally, huge amounts of cotton and sunflower stalks are generated annually. These wastes are being underutilized since they are mostly burned in the fields. So, in this work, we proposed a three-step method consisting of acid pre-treatment, alkaline hydrolysis, and bleaching for the extraction of cellulose pulps. These pulps were characterized to assess their morpho-structural and thermal properties. The design of experiments and response surface methodology were used for the optimization of the acid pre-treatment in order to achieve maximum removal of non-cellulosic compounds and obtain pulps enriched in cellulose. For cotton stalks, optimal conditions were identified as a reaction time of 190 min, a reaction temperature of 96.2 °C, and an acid (nitric acid) concentration of 6.3%. For sunflower stalks, the optimized time, temperature, and acid concentration were 130 min, 73.8 °C, and 8.7%, respectively. The pulps obtained after bleaching contained more than 90% cellulose. However, special care must be taken during the process, especially in the acid pre-treatment, as it causes the solubilization of a great amount of material. The characterization revealed that the extraction process led to cellulose pulps with around 69–70% crystallinity and thermal stability in the range of 340–350 °C, ready to be used for their conversion into derivatives for industrial applications.