In order to investigate the effect of phase separation (PS) on the super duplex stainless steel SAF 2507, the evolution of the nanostructure, mechanical properties, and corrosion resistance of the alloy was studied after aging at 500 °C for 1, 10, 100, and 1000 h. The nanostructure of PS was quantitatively characterized by small-angle neutron scattering. The hardness, impact toughness, and pitting corrosion resistance were measured for different conditions. The results show that the early stage of PS had a more significant impact on the nanostructure and properties of SAF 2507. The fracture behavior of the alloy was likely determined by the mechanical properties of ferrite for aged conditions. The pitting corrosion resistance of SAF 2507 aged at 500 °C was closely related to the Cr depletion caused by PS, and the resistance became weaker with the progression of PS. The evolution of the passivation region with aging time correlated well with that of mechanical properties and characteristic parameters of PS, indicating that it is possible to develop a new nondestructive electrochemical method to quantify the evolution of PS in SAF 2507.

The Laves phase precipitates in ASTM A335 P92 (P92) steel were found to dissolve in solutions with NaOH concentration higher than 7 mol l ⁻¹ . Such behaviour was utilized to detect and quantify the precipitates in P92 specimens aged at 650 °C for times from 0 to 5000 h. The amount of precipitates was acquired by potentiodynamically polarizing the sample and integrating the dissolution current over time. The result was compared to that of a traditional SEM observation method, and a good linear correlation was found between the results. The dissolution mechanism was discussed based on the electrochemical behaviour of an artificially synthesized Fe ₂ Mo laves phase specimen, pure Fe, and pure Mo in the strong alkaline solution.

The Laves phase formed during the long-term creep of 9% Cr heat-resistant steels plays an important role in their high-temperature mechanical properties. Detecting and quantifying the Laves phase is one of the main problems in predicting the creep residual life. This study detects and quantifies the Laves phase in various 9% Cr heat-resistant steel samples by anodic polarization. Both T92/P92 samples after creep and 9Cr ferritic martensitic samples after thermal ageing precipitate Laves phase particles, and the content of the Laves phase increases with the service time. Comparing the results obtained by the electrochemical method with those obtained by the traditional SEM observation method, it can be found that there is a similar two-stage linear relationship between the two results in all materials, which is related to the diameter change of Laves phase particles during service. According to the correlation between the Laves phase content and creep time, an extrapolation method for the prediction of the residual creep life is proposed. The results show that the creep life of P92 can be predicted by using the dissolved charge density of the Laves phase with high prediction accuracy. This method has the potential to evaluate the service states of materials and predict the long-term creep life in the industrial field.