Membranes with tailorable surface chemistry have applications in a wide range of industries. Synthesizing membranes from poly(chloromethyl styrene) directly incorporates an alkyl halide surface-bound initiator which can be used to install functional groups via S_N2 chemistry or graft polymerization techniques. In this work, poly(chloromethyl styrene) membranes were synthesized through electrospinning. After fabrication, membranes were crosslinked with a diamine, and the chemical resistance of the membranes was evaluated by exposure to 10 M nitric acid, ethanol, or tetrahydrofuran for 24 h. The resulting membranes had diameters on the order of 2–5 microns, porosities of >80%, and permeance on the order of 10,000 L/m²/h/bar. Crosslinking the membranes generally increased the chemical stability. The degree of crosslinking was approximated using elemental analysis for nitrogen and ranged from 0.5 to 0.9 N%. The poly(chloromethyl styrene) membrane with the highest degree of crosslinking did not dissolve in THF after 24 h and retained its high permeance after solvent exposure. The presented chemically resistant membranes can serve as a platform technology due to their versatile surface chemistry and can be used in membrane manufacturing techniques that require the membrane to be contacted with organic solvents or monomers. They can also serve as a platform for separations that are performed in strong acids.

Extractive diglycolamide (DGA) resins are used in several state-of-the-art techniques for purifying ²²⁵Ac, a promising radiometal for targeted alpha therapy. Unfortunately, separation processes that rely on resins are often limited to slow flow rates, high elution volumes, and long processing times. Membrane adsorbers functionalized with DGA ligands are an alternative separation material that may overcome these challenges. This work presents (1) the synthesis of an aminated tetrahexyldiglycolamide ligand, (2) the covalent tethering of the ligand to electrospun poly(vinylbenzyl chloride) fiber mats, and (3) the adsorption and desorption of La(III) and ²²⁵Ac. Chemical and physical characterization supports the covalent tethering of the ligand to the fiber mat, as well as the preservation of the fiber surface area and porosity after functionalization. Equilibrium adsorption experiments were performed with stable La(III) and radioactive ²²⁵Ac. Trends in affinity are consistent between commercial resins and the synthesized membrane adsorbers; however, the Langmuir constants and the maximum binding capacity of the membrane adsorbers were generally lower than the resins. Despite these differences, the modeled selectivity for an equimolar solution of La(III)/²²⁵Ac in 10 M nitric acid is 57. Furthermore, ²²⁵Ac is rapidly desorbed from the fibers in 10 M nitric acid (<20 min). The La(III)/²²⁵Ac selectivity and rapid ²²⁵Ac desorption indicate this class of materials is promising for rapid radioanalytical separations.