Bone contains considerable amounts of minerals and proteins. Hydroxyapatite [Ca₁₀(PO₄)₆(OH)₂] is one of the most stable forms of calcium phosphate and it occurs in bones as major component (60 to 65%), along with other materials including collagen, chondroitin sulfate, keratin sulfate and lipids. In recent years, significant progress has been made in organ transplantation, surgical reconstruction and the use of artificial protheses to treat the loss or failure of an organ or bone tissue. Chitosan has played a major role in bone tissue engineering over the last two decades, being a natural polymer obtained from chitin, which forms a major component of crustacean exoskeleton. In recent years, considerable attention has been given to chitosan composite materials and their applications in the field of bone tissue engineering due to its minimal foreign body reactions, an intrinsic antibacterial nature, biocompatibility, biodegradability, and the ability to be molded into various geometries and forms such as porous structures, suitable for cell ingrowth and osteoconduction. The composite of chitosan including hydroxyapatite is very popular because of the biodegradability and biocompatibility in nature. Recently, grafted chitosan natural polymer with carbon nanotubes has been incorporated to increase the mechanical strength of these composites. Chitosan composites are thus emerging as potential materials for artificial bone and bone regeneration in tissue engineering. Herein, the preparation, mechanical properties, chemical interactions and in vitro activity of chitosan composites for bone tissue engineering will be discussed.

To determine the efficacies of antibacterial and antioxidant activities of aqueous leaf extract of Psidium guajava mediated biosynthesis of titanium dioxide nanoparticles (TiO2 NPs). Synthesized TiO2 NPs were tested by disc diffusion method against against human pathogenic bacteria. The total antioxidant activity and phenolic content (Folin-Ciocalteau method) of synthesized TiO2 NPs and aqueous plant extract were determined. The scavenging radicals were estimated by DPPH method. The synthesized TiO2 NPs were characterized by XRD, FTIR, FESEM and EDX. FTIR spectra of synthesized TiO2 NPs exhibited prominent peaks at 3 410 cm(-1) (alkynes), 1 578 cm(-1), 1 451 cm(-1) (alkanes), and 1 123 cm(-1)(C-O absorption). The morphological characterization of synthesized TiO2 NPs was analysed by FESEM which showed spherical shape and clusters with an average size of 32.58 nm. The maximum zone of inhibition was observed in the synthesized TiO2 NPs (20 μg/mL) against Staphylococcus aureus (25 mm) and Escherichia coli (23 mm). The synthesized TiO2 NPs showed more antibacterial activity than the standard antibiotic disk, tetracycline which drastically reduces the chances for the development of antibiotics resistance of bacterial species. The plant aqueous extract and synthesized TiO2 NPs were found to possess maximum antioxidant activity when compared with ascorbic acid. The content of phenolic compounds (mg/g) in leaf aqueous extract and synthesized TiO2 NPs were found to be 85.4 and 18.3 mgTA/g, respectively. Green synthesized TiO2 NPs provides a promising approach can satisfy the requirement of large-scale industrial production bearing the advantage of low-cost, eco-friendly and reproducible.

In recent years, significant development has been achieved in the construction of artificial bone with ceramics, polymers and metals. Nano-hydroxyapatite (nHA) is widely used bioceramic material for bone graft substitute owing to its biocompatibility and osteoconductive properties. nHA with chitin, chitosan, collagen, gelatin, fibrin, polylactic acid, polycaprolactone, poly(lactic- co -glycolic) acid, polyamide, polyvinyl alcohol, polyurethane and polyhydroxybutyrate based composite scaffolds have been explored in the present review for bone graft substitute. This article further reviews the preparative methods, chemical interaction, biocompatibility, biodegradation, alkaline phosphatase activity, mineralization effect, mechanical properties and delivery of nHA-based nanocomposites for bone tissue regeneration. The nHA based composite biomaterials proved to be promising biomaterials for bone tissue engineering.