The combustion characteristics and kinetics of high- and low-reactivity metallurgical cokes in an air atmosphere were studied by thermogravimetric instrument. The Coats–Redfern, FWO, and Vyazovkin integral methods were used to analyze the kinetics of the cokes, and the kinetic parameters of high- and low-reactivity metallurgical cokes were compared. The results show that the heating rate affected the comprehensive combustion index and combustion reaction temperature range of the cokes. The ignition temperature, burnout temperature, combustion characteristics, and maximum weight-loss rate of low-reactivity coke (L-Coke) were better than high-reactivity coke (H-Coke). Low-reactivity coke had better thermal stability and combustion characteristics. At the same time, it was calculated via three kinetic analysis methods that the combustion activation energy gradually decreased with the progress of the reaction. The coke combustion activation energy calculated by the Coats–Redfern method was larger than the coke combustion activation energy calculated by the FWO and Vyazovkin methods, but the laws were consistent. The activation energy of L-Coke was about 4~8 kJ/mol more than that of H-Coke.

Vanadium−titanium magnetite (VTM) is an important raw material for ironmaking under the situation of increasingly demanding scarce resources. To further improve the metallurgical properties of pellets, and to satisfy the requirements of blast furnace slag basicity, finely ground dolomite and limestone have been added to the pellet. In this study, the effect of finely ground dolomite and limestone on the metallurgical properties (green pellet drop strength, cold compression strength, reduction swelling index, and microscopic mineral structure) of VTM pellets were investigated. With the addition of finely ground dolomite and limestone, the drop strength of the green pellet was improved. The effect of adding finely ground limestone was greater than adding finely ground dolomite. Adding more finely ground dolomite and limestone compared to pellets without limestone and dolomite, the cold compression strength was decreased, which was attributed to the decomposition of limestone and dolomite during the induration of pellets. With the addition of dolomite, the reduction swelling index (RSI) increased firstly and then decreased. When the basicity of the pellet was 0.54 to 0.94, the slag phase with the lowest melting point was formed, corresponding to the maximum of the reduction swelling index. For the pellets with added limestone, the reduction swelling of the pellets deteriorated. The reduction index of the pellets increased and reached the maximum (26.6%) at a basicity of 1.54, which belongs to abnormal swelling.