The flocculation–solidification–filter-press combined method is a new type of method for treating waste slurry that combines flocculation and chemical curing with a mechanical filter press. Among these processes, the mechanical filter-press process is key to the efficient disposal of waste engineering slurries by the flocculation–solidification–filter-press combined method. In the mechanical filter-press process, parameters including the initial thickness of filtration mud, the magnitude of filtration pressure, and the duration of press filtration have important impacts on the dewatering and strength after subsequent curing. In this work, a series of laboratory tests were conducted to study the influence of filter-press parameters on flocculated–solidified mud by measuring the properties of treated and cured mud. The test results showed that the initial mud bag thickness is an important factor in the mud treatment effect. As the initial mud bag thickness increases, the greater the water content of the mud at the end of the filter-press process after applying the same amount of time and the same amount of pressure, the lower the post-conservation strength will be. The increase in filtration pressure and filtration time within a certain range can reduce the water content of the mud brick after filtration and significantly improve its shear strength. In the actual process of filtering in the project, the thickness of the initial mud bag should be no more than 140 mm, the filtration pressure is about 0.35 MPa, and the filtration time is suitable for 2 min.

For the massive quantities and negative impacts of dredged mud slurry, its disposal and utilization have become one of the most noticeable issues in the world. In this paper, the flocculation-solidification-high pressure filtration combined method is proposed to effectively dispose of marine mud slurries. The advantages of this method are demonstrated herein in the following three aspects: dewatering performance, material savings, and the shear strength of the treated marine mud slurry. Then, the effects of the anionic polyacrylamide (APAM) dose, composite solidification agent dose, initial water content of marine mud slurries, and initial thickness of geo-bags on the mechanical properties of the marine mud slurry treated by the flocculation-solidification-high pressure filtration combined method are studied. Experimental results show that with increasing doses of APAM, the structures of mud slurries become more stable, and the optimal dose of APAM is determined as 0.16%. Moreover, the increase in the composite solidification agent dose and initial water content of the marine mud slurry, and the decrease in the initial thickness of geo-bags both contribute to the increase in the shear strength of the marine mud slurry treated by the flocculation-solidification-high pressure filtration combined method.