An all-solid-state polymeric membrane potentiometric sensor for sensitive and selective determination of bisphenol S is developed for the first time.

Nowadays, it is still difficult for molecularly imprinted polymers (MIPs) to achieve homogeneous recognition since they cannot be easily dissolved in organic or aqueous phase. To address this issue, soluble molecularly imprinted nanorods have been synthesized by using soluble polyaniline doped with a functionalized organic protonic acid as the polymer matrix. By employing 1-naphthoic acid as a model, the proposed imprinted nanorods exhibit an excellent solubility and good homogeneous recognition ability. The imprinting factor for the soluble imprinted nanoroads is 6.8. The equilibrium dissociation constant and the apparent maximum number of the proposed imprinted nanorods are 248.5 μM and 22.1 μmol/g, respectively. We believe that such imprinted nanorods may provide an appealing substitute for natural receptors in homogeneous recognition related fields.

Lightweight materials with a density less than 3 g/cm³ as potential tribo-materials for tribological applications (e.g., space tribology) are always desired. Al₃BC₃ ceramic, a kind of ternary material, is one of the lightweight materials. In this study, dense Al₃BC₃ ceramic is prepared via a reactive hot-pressing process in a vacuum furnace. Its tribological properties are investigated in two unlubricated conditions (one is at elevated temperature up to 700 °C in air, and another is in a vacuum chamber of back pressures from 10⁵ Pa to 10⁻² Pa at room temperature) and lubricated conditions (i.e., water and ethanol as low-viscosity fluids). At 400 °C and lower temperatures in air, as well as in vacuum, the tribological property of Al₃BC₃ ceramic is poor due to the fracture of grains and formation of a mechanically mixed layer. The beneficial influence of adsorbed gas species on reducing friction is very limited. Due to the formation of lubricious tribo-oxide at 600 °C and 700 °C, the friction coefficient is reduced from ca. 0.9 at room temperature and 400 °C to ca. 0.4. In the presence of low-viscosity fluids, a high friction coefficient and wear but a polished surface are observed in water, while a low friction coefficient and wear occur in ethanol. A lubricious carbide-derived carbon (CDC) coating on top of Al₃BC₃ ceramic through high-temperature chlorination can be fabricated and the wear resistance of CDC can be improved by adjusting the chlorination parameters. The above results suggest that Al₃BC₃ ceramic is a potential lubricating material for some tribological applications.