To improve the shear performance and construction efficiency of horizontal joints in prefabricated concrete wall panel structures, an innovative keyway joint for prefabricated concrete wall panels is presented to maximize the contact area and joint friction, enhancing both the shear performance and the installation efficiency. Shear tests on eight prefabricated concrete wall panels were conducted to investigate the effects of the axial compression ratio, interface mortar strength, and keyway depth on the shear performance of these novel joints. Concurrently, a finite element model for prefabricated concrete wall panel keyway connections was established via ABAQUS, and a parametric analysis approach was employed to study various factors such as the axial compression ratio, the interface mortar strength, and the keyway construction type, as well as their impact on the shear performance of joints. The findings showed that, as the axial compression ratio increased, the failure mode of the keyway joint transitioned from shear brittle failure to compressive shear plastic failure, accompanied by evident crack propagation. The recommended keyway depth parameter remains between 40 and 80 mm, with the inclination angle of the keyway joint ideally ranging from 0° to 20°. Compared to the straight joint, the shear capacity of the innovative keyway joint increased by 16.5%.

Most of the existing studies on acid corrosion of concrete have focused on the mechanical behavior of concrete structures under monotonic load or without load. To investigate the mechanical properties of in-service concrete components under cyclic load in an acid corrosion environment, six groups of concrete prism specimens with different acid corrosion degrees (corrosion duration) were designed and prepared by the accelerated corrosion test method. The monotonic and cyclic axial compression load tests on these specimens were conducted to investigate the effects of corrosion degree on the mechanical properties of concrete specimens. The experimental results indicated that hydrochloric acid corrosion has obvious effects on the failure characteristics and mechanical properties of concrete. The surface of corroded concrete was easier to crack and spall under load, and the concrete spalling area enlarged as the acid corrosion duration increased. The compressive capacity of concrete specimens reduced rapidly with the increase in corrosion duration. The stress–strain envelope curves for concrete with different corrosion duration under cyclic load were essentially similar to that of concrete under monotonic load. The degradation rate of the descending section for the stress–strain curves of corroded concrete under cyclic load was much larger than that under the monotonic load due to the accumulation of internal damage in concrete. The peak strain and ultimate strain of corroded concrete increased significantly with the increase in corrosion duration and enhanced by 55.7% and 77.9%, respectively, compared with the uncorroded concrete, whereas the peak stress and elastic modulus rapidly decreased and reduced by 53.3% and 74.1%, respectively. Moreover, based on the strength degradation depth, the concept of effective bearing cross-sectional area ratio was proposed to characterize the corrosion degree of concrete, and the correction coefficient of descending section for the effective bearing cross-sectional area ratio was introduced to establish the constitutive model of corroded concrete under cyclic load, and the results calculated by this model matched well with the experimental values. The research in this paper can provide the experimental and theoretical basis for seismic life cycle and fatigue redesign of concrete structures in acid corrosion environments or coastal areas.

Metal roof systems were widely utilized in various important buildings; however, cases of wind damage were often observed. In this paper, wind uplift tests of standing seam aluminum magnesium manganese and continuous welded stainless-steel roof systems were conducted, and the wind resistance bearing capacity and mechanical properties of key joints in the two roof systems were compared and analyzed. Strain gauges and displacement sensors were arranged at different structural layers and key nodes of the roof system to compare and analyze the stress and displacement changes. The results showed that the wind resistance capacity of the continuous welded stainless-steel roof system was more than 25% higher than that of the standing seam aluminum magnesium manganese roof system. The stress and displacement of the roof system gradually increased with the increase in wind load. Obvious differences in stress at different positions of the two roof systems were identified. The stress at the roof panel of the roof system was greater than that of other structural layers, and the maximum displacement of the roof panel in the elastic stage could reach more than 97.5 mm. The fitting coefficient between the test and the finite element was 0.976, and the ultimate bearing capacity of Specimen B was 479.64 MPa. The research results of this paper can provide some data support and reference for engineering design and applications.