Photoinduced second harmonic generation (SHG) in Au nanoparticle-deposited ZnO nanocrystallite (NC) films was explored by applying bicolor coherent treatment of a Nd-YAG laser with wavelength 1.06 µm and its SHG. We have established that coexistence of the ZnO and Au nanoparticles gives a substantially larger SHG output with respect to pure ZnO NC deposited on the glass substrate. It was established that the value of the second order susceptibility is about 23 pm V(-1). Better nonlinear optical susceptibilities were obtained during phototreatment at temperatures near 30-35 °C for the Au doped samples. The samples without gold NCs are temperature independent. Generally an increasing temperature leads to a decrease of the optical SHG.

PbO-Sb(2)O(3)-B(2)O(3) glasses mixed with different concentrations of CoO (ranging from 0 to 2.0 mol%) were crystallized. The samples were characterized by x-ray diffraction, scanning electron microscopy and differential scanning calorimetric techniques. The x-ray diffraction and scanning electron microscopic studies have revealed the presence of CoSb(2)O(6), Co(2.33)Sb(0.67)O(4), Pb(5)Sb(2)O(8),Pb(3)(SbO(4))(2), PbB(4)O(7) and Co(3)O(4) crystalline phases in these samples. The DSC studies have indicated the spreading of the crystallization from the inside to the surface of the samples as the concentration of the crystallizing agent is increased. The IR and Raman spectroscopic studies have pointed out the existence of conventional BO(3), BO(4), SbO(4) and also Co(III)-O structural units in the glass ceramic samples. These studies have further indicated the decreasing concentration of symmetrical structural vibrational groups with increase in the concentration of CoO. The results of various studies, namely dielectric properties over a range of frequency and temperature, photo-induced birefringence, optical absorption, fluorescence and magnetic susceptibility at room temperature of PbO-Sb(2)O(3)-B(2)O(3):CoO glass ceramics, have also been reported. The variations observed as a function of the concentration of crystallizing agent in all these properties have been analyzed in the light of different oxidation states and environments of cobalt ions in the glass ceramic network.