Duplex stainless steel multi-pass welds were made at 0.15 MPa, 0.45 MPa, and 0.75 MPa pressure, simulating underwater dry hyperbaric welding by the flux-cored arc welding (FCAW) method, with welds of normal pressure as a benchmark. The purpose of this work was to estimate the effect of ambient pressure on the microstructure, pitting corrosion resistance and impact toughness of the weld metal. The microstructure measurement revealed that the ferrite content in the weld metal made at 0.45 MPa is the lowest, followed by that of 0.75 MPa and 0.15 MPa. The analysis of potentiodynamic polarization tests at 30 °C and 50 °C demonstrated that the pitting corrosion resistance depends on the phases of the lower pitting resistance equivalent numbers (PREN), secondary austenite and ferrite. The weld metal made at 0.45 MPa had the best resistance to pitting corrosion at 30 °C and 50 °C with the highest PRENs of secondary austenite and ferrite. The weld metal made at 0.15 MPa displayed the lowest pitting corrosion resistance at 30 °C with the lowest PREN of secondary austenite, while the weld metal made at 0.75 MPa was the most seriously eroded after being tested at 50 °C for the lowest PREN of ferrite, with large cluster pits seen in ferrite at 50 °C. The impact tests displayed a typical ductile-brittle transition because of the body-centered cubic (BCC) structure of the ferrite when the test temperature was lowered. All the weld metals met the required value of 34 J at −40 °C according to the ASTM A923. The highest ferrite content corresponded to the worst impact toughness, but the highest toughness value did not correspond to the greatest austenite content. With the decreasing of the test temperature, the drop value of absorbed energy was correlated to the ferrite content. Additionally, in this work, the weld metal made at 0.45 MPa had the best combined properties of pitting resistance and impact toughness.

Duplex stainless steel welded metals were underwater local dry prepared on S32101 lean duplex stainless steel trapezoidal groove plates with a self-made drain cover employing Supercore 2205P flux-cored filler wire. Different heat inputs were employed to investigate the effects on mechanical characteristics and the microstructure of welded metals. The results demonstrated that as the heat was applied, austenite concentrations in the weld metals increased. It was found that the austenite concentration and the fraction of Σ3-austenite twin-grain boundaries followed the same trends. With increasing heat input, the recrystallized ferrite and austenite grains initially decreased and subsequently increased, whereas the fraction of interphase boundaries between special ferrite and austenite exhibited the reverse trend. With a heat input of 1.4 kJ/mm, the toughness and plasticity of the weld metals were enhanced by an increase in austenite content, Σ3 recrystallized grains, and austenite twin-grain boundaries. The plasticity and tensile strength values of the welded metal changed more when the heat input was raised from 1.0 to 1.2 kJ/mm than when it was raised from 1.2 to 1.4 kJ/mm. Considering energy conservation, it is recommended to adopt 1.2 kJ/mm for welding heat input.

This study provides a comprehensive review of ultrasonic welding research in molecular dynamics simulations, encompassing the latest advancements by scholars worldwide. Compared to traditional welding methods, ultrasonic welding offers advantages such as faster processing speed, higher mechanical strength, and environmentally friendly characteristics. However, its process parameters are subject to multiple influencing factors. Molecular dynamics simulations enable the detailed visualization of material interactions and structural changes at atomic/molecular levels during ultrasonic welding. These simulations not only predict how different process parameters affect weld quality but also facilitate the rapid identification of viable solutions, thereby reducing experimental iterations and lowering R&D costs. This review delves into the core theoretical issues pertaining to ultrasonic welding, providing robust support for practical applications. Additionally, specific optimization strategies are proposed to enhance welding performance and efficiency, promoting sustainable development in related industries. Future research could focus on exploring ultrasonic welding mechanisms under complex structures and multi-component systems.

To enhance the applicability of dual-phase high-entropy alloys (HEAs) like Fe32Cr33Ni29Al3Ti3, fabricated via laser beam power bed fusion (LB-PBF), a focus on improving their mechanical properties is essential. As part of this effort, heat treatment was explored. This study compares the microstructure and mechanical properties of the as-printed sample with those cooled in water after undergoing heat treatment at temperatures ranging from 1000 to 1200 °C for 1 h. Both pre- and post-treatment samples reveal a dual-phase microstructure comprising FCC and BCC phases. Although heat treatment led to a reduction in tensile and yield strength, it significantly increased ductility compared to the as-printed sample. This strength-ductility trade-off is related to changes in grain sizes with ultrafine grains enhancing strength and micron grains optimizing ductility, also influencing the content of FCC/BCC phases and dislocation density. In particular, the sample heat-treated at 1000 °C for 1 h and then water-cooled exhibited a better combination of strength and ductility, a yield strength of 790 MPa, and an elongation of 13%. This research offers innovative perspectives on crafting dual-phase HEA of Fe32Cr33Ni29Al3Ti3, allowing for tailorable microstructure and mechanical properties through a synergistic approach involving LB-PBF and heat treatment.

To enhance the applicability of dual-phase high-entropy alloys (HEAs) like Fe32Cr33Ni29Al3Ti3, fabricated via selective laser melting (SLM), a focus on improving their mechanical properties is essential. As part of this effort, heat treatment was explored. This study compares the microstructure and mechanical properties of the as-printed sample with those cooled in water after undergoing heat treatment at temperatures ranging from 1000 to 1200 ℃ for 1 hour. Both pre- and post-treatment samples reveal a dual-phase microstructure comprising FCC and BCC phases. Although heat treatment led to a reduction in tensile and yield strength, it significantly increased ductility compared to the as-printed sample. This strength-ductility trade-off is related to changes in grain sizes with ultrafine grains enhancing strength and micron grains optimizing ductility, also the influence of the content of FCC/BCC phases and dislocation density. In particular, the sample heat-treated at 1000 °C for 1 hour and then water-cooled exhibited a better combination of strength and ductility, a yield strength of 790 MPa, and an elongation of 13%. This research offers innovative perspectives on crafting dual-phase HEA of Fe32Cr33Ni29Al3Ti3, allowing for tailorable microstructure and mechanical properties through a synergistic approach involving SLM and heat treatment.