Fast detection of hydrogen gas leakage or its release in different environments, especially in large electric vehicle batteries, is a major challenge for sensing applications. In this study, the morphological, structural, chemical, optical, and electronic characterizations of ZnO:Eu nanowire arrays are reported and discussed in detail. In particular, the influence of different Eu concentrations during electrochemical deposition was investigated together with the sensing properties and mechanism. Surprisingly, by using only 10 μM Eu ions during deposition, the value of the gas response increased by a factor of nearly 130 compared to an undoped ZnO nanowire and we found an H₂ gas response of ∼7860 for a single ZnO:Eu nanowire device. Further, the synthesized nanowire sensors were tested with ultraviolet (UV) light and a range of test gases, showing a UV responsiveness of ∼12.8 and a good selectivity to 100 ppm H₂ gas. A dual-mode nanosensor is shown to detect UV/H₂ gas simultaneously for selective detection of H₂ during UV irradiation and its effect on the sensing mechanism. The nanowire sensing approach here demonstrates the feasibility of using such small devices to detect hydrogen leaks in harsh, small-scale environments, for example, stacked battery packs in mobile applications. In addition, the results obtained are supported through density functional theory-based simulations, which highlight the importance of rare earth nanoparticles on the oxide surface for improved sensitivity and selectivity of gas sensors, even at room temperature, thereby allowing, for instance, lower power consumption and denser deployment.

Zinc oxide (ZnO) is considered to be one of the most explored and reliable sensing materials for UV detection due to its excellent properties, like a wide band gap and high exciton energy. Our current study on a photodetector based on tetrapodal ZnO (t-ZnO) reported an extremely high UV response of ~9200 for 394 nm UV illumination at 25 °C. The t-ZnO network structure and morphology were investigated using XRD and SEM. The sensor showed a UV/visible ratio of ~12 at 25 °C for 394 nm UV illumination and 443 nm visible illumination. By increasing the temperature, monotonic decreases in response and recovery time were observed. By increasing the bias voltage, the response time was found to decrease while the recovery time was increased. The maximum responsivity shifted to higher wavelengths from 394 nm to 400 nm by increasing the operating temperature from 25 °C to 100 °C. The t-ZnO networks exhibited gas-sensing performances at temperatures above 250 °C, and a maximum response of ~1.35 was recorded at 350 °C with a good repeatability and fast recovery in 16 s for 100 ppm of n-butanol vapor. This study demonstrated that t-ZnO networks are good biosensors that can be used for diverse biomedical applications like the sensing of VOCs (volatile organic compounds) and ultraviolet detection under a wide range of temperatures, and may find new possibilities in biosensing applications.

The aim of this study was to develop low-powered, highly selective UV sensor to continuously monitor personalized UV exposure as well as to study annealing effect on UV detection properties of the sensors. ZnO:Al structures were obtained by chemical growth method followed by thermal annealing at 625 °C for 2 h. The studied samples exhibit maximal UV response of 620/488 at 25 °C/50 °C to 370 nm UV radiation before/after annealing, respectively. Thermal annealing of sensor (250 °C for 1 h) led to improvement in fall time from 3860 seconds to 262 seconds at 25 °C and highest responsivity (~48 mA/W) came out for 370 nm wavelength at 75 °C operating temperatures. Consequently, excellent selectivity for 370 nm UV illumination can be ascribed as due to thermal annealing effect which increases the crystallinity, grain size, and roughness of the sensing film. The PL measurements reveals the suppression of structural defects, increase in intensity after annealing and enhanced UV response due to presence of Al content in films. Overall, these structures showed magnificent UV properties, before and especially after additional thermal annealing. UV sensing mechanism of such nanomaterial-based sensor were explained with physio-chemical processes take place on the surface of these structures. The obtained results on annealed ZnO:Al films-based devices is superior to reported performances of other nanostructures, proving new results for UV sensing applications at different operating temperatures in various fields.

The aim of this study was to develop and characterize CuO/Cu2O functionalized with AgPt nanostructures for gas sensing applications. Environmental pollution remains a pressing global concern, requiring effective detection methods. Metal oxide nanostructures, such as those based on copper oxides, offer promising solutions due to their sensitivity and selectivity for various gases. The research investigated the morphology and structure of the nanostructures using techniques such as scanning electron microscopy (SEM), X-ray diffraction (XRD), and Raman spectroscopy. In addition, the nanostructures were functionalized with noble metals such as silver and platinum to enhance their sensory properties. The deposition of polymer layers has been investigated as a method to improve sensor selectivity. The gas sensing properties of the CuO/Cu2O/AgPt nanostructures were evaluated using the Keithley 2400 source meter and showed high sensitivity to gases such as propanol, acetone, hydrogen, and ammonia at elevated temperatures. The results showed that higher operating temperatures result in faster response and recovery times. In addition, the nanostructures exhibited saturation in response at higher concentrations of certain gases. These results highlighted the potential of CuO/Cu2O/AgPt nanostructures in environmental monitoring applications, particularly in industries prone to gas emissions. Overall, this research contributes to the advancement of gas sensing technology for pollution prevention and control efforts.