Thermoresponsive chitosan-graft-poly(N-isopropylacrylamide) (CS-g-PNIPAAm) copolymers of different composition were synthesized by free-radical polymerization of chitosan (CS) and N-isopropylacrylamide (NIPAAm) in aqueous solution using potassium persulfate (PPS) as an initiator. By changing the molar ratio of CS:NIPAAm from 1:0.25 to 1:10 graft copolymers with a CS backbone and different amounts of PNIPAM side chains were prepared. The chemical structure of the obtained CS-g-PNIPAAm copolymers was confirmed by FTIR and ¹H NMR spectroscopy. ¹H NMR spectra were also used to calculate the content of attached PNIPAAm side chains. Moreover, the lower critical solution temperature (LCST) behavior of synthesized copolymers was assessed by cloud point, differential scanning calorimetry and particle size measurements. The aqueous solutions of copolymers containing ≥12 molar percent of PNIPAAm side chains demonstrated LCST behavior with the phase separation at around 29.0–32.7 °C. The intensity of thermoresponsiveness depended on the composition of copolymers and increased with increasing content of poly(N-isopropylacrylamide) moieties. The synthesized thermoresponsive chitosan-graft-poly(N-isopropylacrylamide) copolymers could be potentially applied in drug delivery systems or tissue engineering.

Polymer flocculants are used to promote solid–liquid separation processes in wastewater treatment technologies, and bio-based flocculants possess many advantages over conventional synthetic polymers. Potato starch microgranules were chemically modified and mechanically sheared to produce modified starch flocculants. The effectiveness of produced cationic starch (CS) and cross-linked cationic starch (CCS) flocculants in the thickening and dewatering of surplus activated sewage sludge was evaluated and compared with that of synthetic cationic flocculants (SCFs) The flocculation efficiency of SCF, CS, and CCS in sludge thickening was determined by measuring the filtration rate of treated surplus activated sludge. Comparing the optimal dose of SCFs and CCS flocculants needed for thickening, the CCS dose was more than 10 times higher, but a wide flocculation window was determined. The impact of used flocculants on the dewatering performance of surplus activated sludge at optimal dose conditions was investigated by measuring capillary suction time. The filtration efficiencies (dewaterability) of surplus activated sludge using SCF, CS, and CCS were 69, 67, and 72%, respectively. The study results imply that mechanically processed cross-linked cationic starch has a great potential to be used as an alternative green flocculant in surplus activated sludge thickening and dewatering operations in municipal sewage sludge treatment processes.

Cereals are subject to contamination by pathogenic fungi, which damage grains and threaten public health with their mycotoxins. Fusarium graminearum and its mycotoxins, trichothecenes B (TCTBs), are especially targeted in this study. Recently, the increased public and political awareness concerning environmental issues tends to limit the use of traditional fungicides against these pathogens in favor of eco-friendlier alternatives. This study focuses on the development of biofungicides based on the encapsulation of a curcumin derivative, tetrahydrocurcumin (THC), in polysaccharide matrices. Starch octenylsuccinate (OSA-starch) and chitosan have been chosen since they are generally recognized as safe. THC has been successfully trapped into particles obtained through a spray-drying or freeze-drying processes. The particles present different properties, as revealed by visual observations and scanning electron microscopy. They are also different in terms of the amount and the release of encapsulated THC. Although freeze-dried OSA-starch has better trapped THC, it seems less able to protect the phenolic compound than spray-dried particles. Chitosan particles, both spray-dried and lyophilized, have shown promising antifungal properties. The IC₅₀ of THC-loaded spray-dried chitosan particles is as low as 0.6 ± 0.3 g/L. These particles have also significantly decreased the accumulation of TCTBs by 39%.

Arthrospira platensis is a filamentous cyanobacterium produced commercially for human consumption, and it is a source of phycocyanin (PC), which recently stirred up great interest due to its anti-inflammatory, radical scavenging, antioxidant and hepato-protective properties. This work has studied the encapsulation of A. platensis extract in starch sodium octenyl succinate by employing freeze-drying and two spray-drying techniques, conventional and nanospray-drying. The main characteristics and properties, including PC encapsulation efficiency, size, colour, and thermal stability of the capsules, were evaluated. Moreover, the antioxidant capacity of encapsulated extract and release of PCs into saliva simulant, were studied and compared. Similar PC encapsulation efficiency was achieved using freeze-drying and nanospray-drying techniques with values of 67–71% and 70–78%, respectively. Meanwhile, the conventional spray-drying method achieved significantly lower encapsulation efficiency values (38–42%). The thermal stability of encapsulated A. platensis extract was improved as demonstrated by the higher decomposition temperature, which was increased by 8–11 °C, 11–15 °C, and 22–23 °C for spray-dried, nanospray-dried and freeze-dried samples, respectively. The nanospray-drying technique allowed the production of the smallest particles with an average diameter of 2–14 µm, good colour and thermal stability, and antioxidant capacity. Overall, the results demonstrated the potential of A. platensis extract encapsulation in modified starch using several techniques with potential application as bioactive ingredients in nutraceutical or pharmaceutical products.