Significance: Two-dimensional transition metal carbides (MXenes) offer a quite unique combination of excellent mechanical properties, hydrophilic surfaces, and metallic conductivity. In this first report (to our knowledge) on MXene composites of any kind, we show that adding polymer binders/spacers between atomically thin MXenes layers or reinforcing polymers with MXenes results in composite films that have excellent flexibility, good tensile and compressive strengths, and electrical conductivity that can be adjusted over a wide range. The volumetric capacitances of freestanding Ti ₃ C ₂ T _x MXene and its composite films exceed all previously published results. Owing to their mechanical strength and impressive capacitive performance, these films have the potential to be used for structural energy storage devices, electrochemical actuators, radiofrequency shielding, among other applications.

Nanometer-thin sheets of 2D Ti₃C₂T_x (MXene) have been assembled into freestanding or supported membranes for the charge- and size-selective rejection of ions and molecules. MXene membranes with controllable thicknesses ranging from hundreds of nanometers to several micrometers exhibited flexibility, high mechanical strength, hydrophilic surfaces, and electrical conductivity that render them promising for separation applications. Micrometer-thick MXene membranes demonstrated ultrafast water flux of 37.4 L/(Bar·h·m²) and differential sieving of salts depending on both the hydration radius and charge of the ions. Cations with a larger charge and hydration radii smaller than the interlayer spacing of MXene (∼6 Å) demonstrate an order of magnitude slower permeation compared to single-charged cations. Our findings may open a door for developing efficient and highly selective separation membranes from 2D carbides.

Tailor-made edge site-enriched inorganics coupled graphene hybrids hold a promising platform material for high-performance supercapacitors. Herein, we report a simple strategy for fabricating edge site-enriched nickel–cobalt sulfide (Ni–Co–S) nanoparticles decorated on graphene frameworks to form integrated hybrid architectures (Ni–Co–S/G) via an in situ chemically converted method. The Kirkendall effect-involved anion exchange reaction, e.g. the etching-like effort of the S²⁻ ions, plays a crucial role for the formation of the edge site-enriched nanostructure. Density functional theory (DFT) calculations reveal that the Ni–Co–S edge sites have a high electrochemical activity and strong affinity for OH⁻ in the electrolyte, which are responsible for the enhanced electrochemical performance. Benefiting from the integrated structures of Ni–Co–S nanoparticles and conductive graphene substrates, the resultant Ni–Co–S/G hybrid electrodes exhibit a high specific capacitance of 1492 F g⁻¹ at the current density of 1 A g⁻¹, a superior rate capability of 96% when the current density is increased to 50 A g⁻¹, and excellent electrochemical stabilities. An asymmetric supercapacitor fabricated using the edge site-enriched Ni–Co–S/G hybrids as the positive electrode and porous carbon nanosheets (PCNS) as negative electrodes shows a high energy density of 43.3 W h kg⁻¹ at a power density of 0.8 kW kg⁻¹, and an energy density of 28.4 W h kg⁻¹ can be retained even at a high power density of 22.1 kW kg⁻¹.