Graphene oxide–iron oxide (GO–Fe3O4) nanocomposites were synthesised by co-precipitating iron salts onto GO sheets in basic solution. The results showed that formation of two distinct structures was dependent upon the GO loading. The first structure corresponds to a low GO loading up to 10 wt%, associated with the beneficial intercalation of GO within Fe3O4 nanoparticles and resulting in higher surface area up to 409 m2 g−1. High GO loading beyond 10 wt% led to the aggregation of Fe3O4 nanoparticles and the undesirable stacking of GO sheets. The presence of strong interfacial interactions (Fe-O-C bonds) between both components at low GO loading lead to 20% higher degradation of Acid Orange 7 than the Fe3O4 nanoparticles in heterogeneous Fenton-like reaction. This behaviour was attributed to synergistic structural and functional effect of the combined GO and Fe3O4 nanoparticles.

GO–Fe₃O₄ confers superior catalytic efficiency, recyclability and longevity, via the oxidation of CC bonds, thus transferring electrons to Fe₃O₄.

Double perovskite Ba₂Bi_0.1Sc_0.2Co_1.7O_6−x (BBSC) demonstrates low polarization resistance between 600 and 750 °C due to the high oxygen reduction rate of BBSC as reflected by its large D_V and k values, which are derived from the face centered cubic structure and high cobalt content.