The adsorption of Eu(III) on composites synthesised from graphene oxide (GO), maghemite (MGH), and chitosan (CS) has been studied using different approaches. The physicochemical and morphological characteristics of the composites GO-MGH, GO-CS, GO-MGH-CS I, II, and III were determined by XRD, Mössbauer spectroscopy, FTIR, Raman spectroscopy, and TEM. According to the results of batch experiments, the maximum experimental adsorption capacity was 52, 54, 25, 103, and 102 mg/g for GO-MGH, GO-CS, GO-MGH-CS I, II, and III, respectively. The data obtained are in better agreement with the Langmuir, pseudo-second-order, and pseudo-first-order models only for GO-MGH. Thus, the adsorption of Eu(III) on the composites was a favourable, monolayer, and occurred at homogeneous sites. The nature of adsorption is chemical and, in the case of GO-MGH, physical. Tests of the composites in natural waters showed a high removal efficiency for Eu(III), Pu(IV), and Am(III), ranging from 74 to 100%. The ANFIS model has quite good predictive ability, as shown by the values for R², MSE, SSE, and ARE. The GO-MGH-CS composites with the high adsorption capacity could be promising candidates for the removal of Eu(III) and the pre-concentration of Pu(IV) and Am(III) from natural waters.

In this study, a highly crystalline bismuth ferrite (BFO) powder was synthesized using a novel, very simple, and cost-effective synthetic approach. It was demonstrated that the optimal annealing temperature for the preparation of highly-pure BFO is 650 °C. At lower or higher temperatures, the formation of neighboring crystal phases was observed. The thermal behavior of BFO precursor gel was investigated by thermogravimetric and differential scanning calorimetry (TG-DSC) measurements. X-ray diffraction (XRD) analysis and Mössbauer spectroscopy were employed for the investigation of structural properties. Scanning electron microscopy (SEM) was used to evaluate morphological features of the synthesized materials. The obtained powders were also characterized by magnetization measurements, which showed antiferromagnetic behavior of BFO powders.

The present study investigates thermally induced crystallization and phase evolution of amorphous calcium phosphate (ACP) partially substituted with Fe ³⁺ ions (M/P = 1.5 : 1).

In this study, an environmentally friendly sol-gel synthetic approach was used for the preparation of yttrium-doped MgFe₂O₄. Two series of compounds with different iron content were synthesized and A-site substitution effects were investigated. In the first series, the iron content was fixed and the charge balance was suggested to be compensated by a partial reduction of Fe³⁺ to Fe²⁺ or formation of interstitial O²⁻ ions. For the second series of samples, the iron content was reduced in accordance with the substitution level to compensate for the excess of positive charge, which accumulates due to replacing divalent Mg²⁺ with trivalent Y³⁺ ions. Structural, morphological and magnetic properties were inspected. It was observed that single-phase compounds can only form when the substitution level reaches 20 mol% of Y³⁺ ions and iron content is reduced. The coercivity as well as saturation magnetization decreased with the increase in yttrium content. Mössbauer spectroscopy was used to investigate the iron content in both tetrahedral and octahedral positions.