Developing advanced underwater welding technology for titanium, which is the key structural material for underwater applications, is of great significance for the design, fabrication, and maintenance of submarine equipment. In this study, in order to investigate the underwater welding microstructure and mechanical properties of Ti-4Al-2V alloy, underwater wet laser welding was conducted on Ti-4Al-2V alloy using varying laser power. The microstructure and properties of the welding joints were characterized and analyzed. The microstructure of the heat-affected zone and fusion zone in the welding joints are not significantly different from those of welding in air, but a mixed oxide layer composed of Al₂O₃ and TiO₂ is formed on the surface of the fusion zone. Due to internal stress, a large number of cracks initiate on the oxide layer and propagate to the joints. In the 4 kW and 5 kW joints, a penetrating crack formed due to the excessive accumulation of internal stress breaking up the α phase. The mechanical properties of the joints are significantly affected by the laser power. The tensile strength of the 3 kW and 4 kW joints is comparable to that of the base metal, which is about 600 MPa, while the 5 kW joint shows brittle fracture with no plastic deformation and 228 MPa strength. This research lays a solid foundation for understanding the underwater wet laser welding behavior of titanium alloys.

Laser welding of the near α-phase titanium alloy Ti-4Al-2V, used for complex components in the nuclear industry, has been rarely reported. In this study, butt weld joints made of Ti-4Al-2V alloy plates under different parameters, including the laser power, the welding speed, and the defocus distance, were manufactured and analyzed. The results showed that adjusting the combination of 4.2 kW of laser power, a 20 mm/s welding speed, and a −2 mm defocus distance could achieve a penetration depth exceeding 6 mm. Porosity defects were prone to forming in the middle and bottom parts of the fusion zone, due to rapid cooling. The microstructure of the fusion zone was mainly needle-like α martensite, which precipitated in the form of specific clusters. The interior of a cluster was composed of three types of variants with /60° phase interfaces to achieve the lower boundary’s energy. Affected by the microstructure and welding defects, the strength of the weld joint was basically similar under different welding conditions, namely about 720 MPa, slightly higher than that of the base metal, while the rupture elongation at breaking decreased by more than 50%. The micro-Vickers hardness of the weld joints was about 50–60 HV higher than that of the base metal, while the impact toughness was about 40 KJ, almost half that of the base metal. This research lays a solid foundation for the engineering application of laser welding of Ti-4Al-2V alloys.