Tissue engineering approaches utilize both natural and synthetic materials in the repair and regeneration processes. A naturally sourced material for this purpose is required to be free from any antigenic matter such as cells or cellular components. Decellularization of tissues may be achieved through chemical or physical removal agents. Supercritical carbon dioxide (sc-CO₂) has been used on the purpose of removing bioburden from tissues and offers an alternative to the traditionally used treatment methods. In addition to many advantages it offers with regard to the successful decellularization of tissues, it is known to have a sterilization effect. This study provides an insight into sc-CO₂–assisted decellularization trials of corneal and aortic tissues. Results showed that high pressure of the fluid bursts the cells during the treatment and rapid depressurization was found to be effective in the removal of the cells from the tissues. sc-CO₂ decellularization offers significantly reduced treatment times, complete decellularization, and preserved extracellular matrix structure.

Poly(glycerol-sebacate) (PGS) was introduced a decade ago as a potential material for soft tissue repair. All of the proposed copolymerization reactions in the literature include a two-stage (prepolymerization and curing) synthesis where the reaction times can take as long as several days. This study, on the other hand, proposes a new route that eliminates these disadvantages and enables a rapid synthesis of PGS elastomers via microwave-assisted prepolymerization in minutes instead of days. No purge gas, catalyst or vacuum is needed in the first prepolymerization step. The curing stage was carried out at 150 °C for 4, 8, 16, and 24 hours. The glass transition temperature (T_g) and melting temperatures for the glycerol and sebacic acid fragments (T m₁ and T m₂ ) of these PGS elastomers were found as −35.61 °C, −15.82 °C, and 61.70 °C, respectively. The Young's modulus and tensile strength values were found as 0.50 ± 0.02 MPa and 0.27 ± 0.06 MPa, respectively.