Organic semiconductor materials are interesting due to their application in various organic electronics devices. [1]benzothieno[3,2-b][1]benzothiophene (BTBT) is a widely used building block for the creation of such materials. In this work, three novel solution-processable regioisomeric derivatives of BTBT—2,7-bis(3-octylthiophene-2-yl)BTBT (1), 2,7-bis(4-octylthiophene-2-yl)BTBT (2), and 2,7-bis(5-octylthiophene-2-yl)BTBT (3)—were synthesized and investigated. Their optoelectronic properties were characterized experimentally by ultraviolet–visible and fluorescence spectroscopy, time-resolved fluorimetry, and cyclic voltammetry and studied theoretically by Time-Dependent Density Functional Theory calculations. Their thermal properties were investigated by a thermogravimetric analysis, differential scanning calorimetry, polarizing optical microscopy, and in situ small-/wide-angle X-ray scattering measurements. It was shown that the introduction of alkyl substituents at different positions (3, 4, or 5) of thiophene moieties attached to a BTBT fragment significantly influences the optoelectronic properties, thermal stability, and phase behavior of the materials. Thin films of each compound were obtained by drop-casting, spin-coating and doctor blade techniques and used as active layers for organic field-effect transistors. All the OFETs exhibited p-channel characteristics under ambient conditions, while compound 3 showed the best electrical performance with a charge carrier mobility up to 1.1 cm²·V⁻¹s⁻¹ and current on/off ratio above 10⁷.

Among short donor–acceptor molecules with a central benzothiadiazole fragment, 4,7-di-2-thienyl-2,1,3-benzothiadiazole (T-BTD) is one of the most well-known compounds, valued for its photophysical and semiconductor properties. We have synthesized a derivative of 4,7-di-2-thienyl-2,1,3-benzothiadiazole with trimethylsilyl end-substituents, 4,7-bis(5-(trimethylsilyl)thiophen-2-yl)benzothiadiazole (TMS-T-BTD). The phase transition parameters and thermal stability of T-BTD and TMS-T-BTD were investigated using DSC and TGA methods. The presence of the trimethylsilyl end-groups in TMS-T-BTD significantly enhances solubility, increases the melting temperature, and improves the resistance of TMS-T-BTD to evaporation in the liquid state. Single crystals of T-BTD and TMS-T-BTD were grown from solutions, with the largest sizes being 7 × 2 × 0.5 mm³ and 8 × 1 × 0.45 mm³, respectively. Using single-crystal X-ray diffraction at 293 K, the crystal structure of T-BTD was refined in the rhombic system (sp.gr. P_cab, Z = 8), while for TMS-T-BTD, it was determined for the first time in the monoclinic system (sp.gr. P2₁/c, Z = 4). The relationship between observed growth anisotropy and molecular packing in the crystals was analyzed. The results of investigations into the spectral-fluorescent properties of solutions in hexane and THF are presented. The solvatochromic effect was studied in a series of solvents, including hexane, THF, dichloromethane, and acetonitrile. The photostability of the compounds in hexane solutions was examined. It was found that the quantum yield of photodestruction for T-BTD is 13 times higher than that of TMS-T-BTD. The fluorescent properties of T-BTD and TMS-T-BTD crystals were investigated.