Since its discovery in 1954, the omega (ω) phase in titanium and its alloys has attracted substantial attention from researchers. The β-to-ω and ω-to-α phase transformations are central to β-titanium alloy design, but the transformation mechanisms have been a subject of debate. With new generations of aberration-corrected transmission electron microscopy and atom probe tomography, both the spatial resolution and compositional sensitivity of phase transformation analysis have been rapidly improving. This review provides a detailed assessment of the new understanding gained and related debates in this field enabled by advanced characterization methods. Specifically, new insights into the possibility of a coupled diffusional-displacive component in the β-to-ω transformation and key nucleation driving forces for the ω-assisted α phase formation are discussed. Additionally, the influence of ω phase on the mechanical properties of β-titanium alloys is also reviewed. Finally, a perspective on open questions and future direction for research is discussed.

The deformation behaviour of an α + β Ti–6Al–4V (wt.%) alloy was investigated during in situ deformation inside a scanning electron microscopy (SEM). Tensile experiments were performed at 296 and 728 K (~0.4Tm), while a tensile-creep experiment was performed at 728 K and 310 MPa (σ/σ_ys = 0.74). The active deformation systems were identified using electron backscattered diffraction-based slip-trace analysis and SEM images of the specimen surface. The distribution of the active deformation systems varied as a function of temperature. Basal slip deformation played a major role in the tensile deformation behaviour, and the relative activity of basal slip increased with increasing temperature. For the 296 K tension deformation, basal slip was less active than prismatic slip, whereas this was reversed at 728 K. Twinning was observed in both the 296 and 728 K tension experiments; however, no more than 4% of the total deformation systems observed was twins. The tension-creep experiment revealed no slip traces, however grain boundary ledge formation was observed, suggesting that grain boundary sliding was an active deformation mechanism. The results of this work were compared with those from previous studies on commercially pure Ti, Ti–5Al–2.5Sn (wt.%) and Ti–8Al–1Mo–1V (wt.%), and the effects of alloying on the deformation behaviour are discussed. The relative amount of basal slip activity increased with increasing Al content.