Electrocatalytic water splitting is one of the most efficient ways of producing green hydrogen energy. The design of stable, active, and efficient electrocatalysts plays a crucial role in water splitting for achieving efficient energy conversion from electrical to hydrogen energy, aimed at solving the lingering energy crisis. In this work, CNT composites modified with CoP-V₄P₃ composites (CoVO-10-CNT-450P) were formed by carbonising a pencil-like precursor (Co₃V₂O₈-H₂O) and growing carbon nanotubes in situ, followed by in situ phosphorylation on the carbon nanotubes. In the HER electrocatalytic process, an overpotential of only 124 mV was exhibited at a current density of 10 mA cm⁻². In addition, as an OER catalyst, a low overpotential of 280 mV was attained at a current density of 10 mA cm⁻². Moreover, there was no noticeable change in the performance of the catalyst over a 90 h test in a continuous total water splitting experiment. The unique electronic structure and hollow carbon nanotube structure of CoVO-10-CNT-450P effectively increased the catalytic active sites, while also significantly improving the electrocatalytic activity. This work provides theoretical guidance for the design and synthetic route of high-performance non-precious metal electrocatalysts, and actively promotes the commercial application of electrochemical water splitting.

The ubiquitous presence of tetracycline in water sources due to its prevalent usage in antibiotics poses a potential risk to ecosystems and to human health. There is therefore a dire need for efficient methods of tetracycline removal. To this end, we constructed a series of super-small-sized BiVO₄ composites with different loading amounts of 5 wt%, 10 wt%, 15 wt%, 20 wt%, and 25 wt% on SiO₂ support by a hydrothermal–calcination method for efficient photocatalytic degradation of tetracycline. XRD and SEM results revealed that these composites all exhibited good crystallinity and well-dispersed morphologies. Particularly, the 20 wt% BiVO₄@SiO₂ of this series of composites showed superior photocatalytic performance, with 84.1% efficiency in tetracycline degradation, higher than any of its counterparts. This can be explained by its wide light-absorption range and high charge-separation efficiency, as confirmed by UV-Vis absorption spectra and quenched fluorescence spectra. This work offers a new method for the design and construction of tetracycline degradation photocatalysts.