Synthesis of a homologous series of photo-polymerizable α,w-polytetrahydrofuranether-diacrylate (PTHF-DA) resins is described with characterization by NMR, GPC, DSC, soaking and rheometrical measurements. The curing speeds of the resins are determined under UV light exposure. Young’s modulus and tensile strength of fully cured resins show flexible to soft material attributes dependent on the molar mass of the used linear PTHF-diacrylates. Structuring the materials by stereo lithography (SL) and multiphoton polymerization (MPP) leads to tubes and bifurcated tube systems with a diameter smaller than 2 mm aimed at small to smallest supplying systems with capillary dimensions. WST-1 biocompatibility tests ofm polymer extracts show nontoxic characteristics of the adapted polymers after a washing process. Some polymers show shape memory effect (SME).

Polarization-electric field hysteresis is an important property of ferroelectric materials. Different experimental procedures and measurement regimes are demonstrated and frequently used in order to determine this hysteresis behavior. For the characterization of the poling behavior of ferroelectric polymers it is common to analyze the poling current and separate current contributions, which are based on charging the sample capacitance as well as on conductivity. Experimentally this can be realized with two different measurement regimes, either poling of the sample with bipolar cycles or with a sequence of bipolar and unipolar cycles of the applied electric field. Here, we demonstrate the comparison of both measurement routines by performing poling experiments on the same ferroelectric PVDF sample.

Cellular polymer films are frequently employed for packaging, insulation, and printing. They can also be used as ferroelectrets in transducer applications. Here, we propose a preparation process for cellular polyethylene-naphthalate (PEN) films with the following steps: (1) foaming by means of supercritical carbon dioxide (CO ₂ ), (2) controlled inflation through gas diffusion and expansion, and (3) biaxial stretching. We describe and assess the cellular structure that is formed under suitable processing conditions. For foaming, the PEN films are saturated with supercritical CO ₂ at room temperature for a few hours, at a pressure as high as 100 bar. The subsequent temperature treatment is very critical for controlling the sample density. Additional inflation can improve the cellular geometry and higher stabilization temperatures during the inflation process cause stronger inflation and thus lower densities. Stretching may be employed in order to achieve a regular cellular structure with lens-like voids. High electromechanical responses, i.e. large piezoelectric thickness coefficients are found only on samples within the proper density range and with optimal cellular structures

The conductivity of α-polyvinylidene fluoride is obtained from dielectric measurements performed in the frequency domain at several temperatures. At temperatures above the glass-transition, the conductivity can be interpreted as an ionic conductivity, which confirms earlier results reported in the literature. Our investigation shows that the observed ionic conductivity is closely related to the amorphous phase of the polymer.