Currently, laser surface treatment (LST) is considered the most promising method available within the industry. It delivers precise control over surface topography, morphology, wettability, and chemistry, making the technique suitable for regulating the corrosion behavior of alloys. In this paper, femtosecond laser texturing with different parameters and atmosphere environments was adopted to clarify the effect of surface treatment on the corrosion resistance of selective laser melted (SLM-ed) 17-4PH stainless steel (SS) in a NaCl solution. The experimental results show that, after the heat treatment, the corrosion resistance of the laser-treated samples was enhanced. With the further laser treatment in an argon atmosphere, the oxidation of nanostructural surfaces was avoided. The Cr, Cu, and other alloying elements precipitated on the laser-ablated surface were beneficial to the formation of a passivation film, leading to an improved corrosion resistance performance.

The rusting of metals brings huge losses to the industry every year, and post-treatment of rusted metals to restore their properties to the initial state is a hot topic of current research. In particular, 20 steel, which is widely used in various structural components such as ships, is prone to oxidation in atmospheric environment. Therefore, in this study, a nanosecond pulsed laser was used to remove the rust layer on the surface of 20 steel. The effects of different energy densities and spot overlap rates on the roughness, surface morphology, chemical composition, microhardness and corrosion resistance of the rust layer were analyzed. The results showed that the best cleaning effect was achieved at an energy density of 4.26 J/cm² and a spot overlap rate of 75%. Under these conditions, the rust layer was completely removed without damage to the substrate, and it even improved the corrosion resistance of 20 steel. At energy densities of 1.42 J/cm² and 2.84 J/cm², the rust layer was not completely removed, while at 5.68 J/cm², the rust layer was removed but the substrate was damaged. In addition, the mechanism of rust removal and substrate damage is discussed.

The process of forming metal components through selective laser melting (SLM) results in inherent spherical effects, powder adhesion, and step effects, which collectively lead to surface roughness in stainless steel, limiting its potential for high-end applications. This study utilizes a laser-electrochemical hybrid process to polish SLM-formed 316L stainless steel (SS) and examines the influence of process parameters such as laser power and scanning speed on surface roughness and micro-morphology. A comparative analysis of the surface roughness, microstructure, and wear resistance of SLM-formed 316L SS polished using laser, electrochemical, and laser-electrochemical hybrid processes is presented. The findings demonstrate that, compared to laser and electrochemical polishing alone, the laser-electrochemical hybrid polishing exhibits the most significant improvement in surface roughness and the highest material wear resistance. Additionally, the hybrid process results in a surface free of cracks and only a small number of tiny corrosion holes, making it more suitable for polishing the surface of 316L SS parts manufactured via SLM.

Titanium alloy components often experience damage from impact loads during usage, which makes improving the mechanical properties of TC4 titanium alloys crucial. This paper investigates the influence of laser scanning irradiation on the tensile properties of thin titanium alloy sheets. Results indicate that the tensile strength of thin titanium alloy sheets exhibits a trend of initial increase followed by a decrease. Different levels of enhancement are observed in the elongation at break of a cross-section. Optimal improvement in the elongation at break is achieved when the laser fluence is around 8 J/cm², while the maximum increase in tensile strength occurs at approximately 10 J/cm². Using femtosecond laser surface irradiation, this study compares the maximum enhancement in the tensile strength of titanium alloy base materials, which is approximately 8.54%, and the maximum increase in elongation at break, which reaches 25.61%. In addition, the results verify that cracks in tensile fractures of TC4 start from the middle, while laser-induced fracture cracks occur from both ends.

To improve the open-loop control performance of stepper motors, research was conducted on their operating curves. The acceleration-velocity characteristic equations of three common operating curves were established and compared with the torque frequency characteristic curves of stepper motors. Based on this, an improved segmented correction fitting S-shaped (SCFS) curve design method based on a high torque utilization sine curve was proposed to solve the problem of rotor blockage and overshoot caused by uneven acceleration during the operation of stepper motors. In the simulation of the stepper motor load motion system, the SCFS curve was compared with common curves. The simulation results showed that the position tracking error was reduced by approximately 82% compared to the trapezoidal curve and approximately 70% compared to the exponential curve. Research has found that this method is suitable for the design of high-precision motor operating curves and has a high application value in the field of precision motion control.