Porous N-doped carbons hold good prospects for application in supercapacitor due to their low-cost, large surface area, good surface wettability, high electrical conductivity as well as extra pseudocapacitance. However, most synthetic methods required the tedious and multiple-step process with the assistance of hard/soft templates or the massive use of chemical reagents, and exogenous nitrogen sources, which made them difficult to realize industrial production and application. Here, we described a novel hierarchical porous N-doped carbons fabricated by a facile and sustainable approach via hydrothermal treatment and subsequent carbonization process by using renewable bamboo shoots as the starting material without any templates, additional chemical activation and nitrogen source. The obtained bamboo shoot-derived carbons possessed a large BET surface area (up to 972 m² g⁻¹), hierarchically interconnected porous framework, rich and uniform nitrogen incorporation (3.0 at%). Benefiting from these unique features, the novel carbon-based electrode materials displayed a high capacitance of 412 F g⁻¹ in KOH electrolyte and long cycling life stability. Thus, an advanced electrode material for high-performance supercapacitor was successfully assembled by a simple and scalable synthesis route with abundant renewable resources freely available in nature.

The search for green and sustainable modification method to produce durable bamboo materials remains a challenge in industry. Here, heat treatment in tung oil at 100–200 °C was employed to modify bamboo materials. Oil permeation and distribution in the structure of bamboo samples during heat treatment were explored. The synergistic effects of tung oil and heat treatment on the chemical, physical and mechanical properties of bamboo materials, and their mutual relationships were also investigated in detail. Results showed that the tung oil heat treated bamboo not only had an enhanced hydrophobic property and dimensional stability, improved fungi resistance, but also displayed good mechanical performance. Compared with the untreated sample, the water-saturated swelling reduced from 3.17% to 2.42% for the sample after oil heat treatment at 200 °C, and the contact angles of the sample after oil heat treatment at 200 °C can keep >100° after 300 s in radial direction. Such improvement can be attributed to changes of chemical components, increased crystallinity structure, and the formation of oily films inside or over the bamboo surface. Therefore, tung oil heat treatment can be a highly promising technology for bamboo modification in the industry.