Pyrrole (Py) is easily agglomerated during the polymerization process, affecting its performance. In this paper, polypyrrole/monodispersed latex sphere (PPy/MLS) composites were prepared using in-situ polymerization for the adsorption of hexavalent chromium (Cr(VI)). The specific surface area of PPy/MLS (39.30 m²/g) was increased relative to that of PPy (24.82 m²/g), thus providing more effective adsorption sites. In addition, the adsorption properties of Cr(VI) under different conditions, including Py content, pH of the aqueous solution, and PPy/MLS dosage, were investigated to reveal the adsorption mechanism. The results showed that PPy/MLS possessed high Cr(VI) adsorption capacities when the Py content was 50 wt %. The maximum adsorption capacity was 343.64 mg/g at pH 2.0 and 25 °C. Remarkably, the adsorbents exhibited an excellent removal rate of Cr(VI) after three cycles of adsorption–desorption (over 99%), suggesting that the adsorbents had exceptional recyclability. Furthermore, the adsorption process followed quasi-second-order kinetics and Langmuir isothermal adsorption model. The high adsorption performance, sustainability, and cost-efficiency make this adsorbent a promising candidate for large-scale Cr(VI) contaminant removal.

Surface-functionalized polymeric microspheres have wide applications in various areas. Herein, monodisperse poly(styrene–methyl methacrylate–acrylic acid) (PSMA) microspheres were prepared via emulsion polymerization. Polyaniline (PANI) was then coated on the PSMA surface via in situ polymerization, and a three-dimensional (3D) structured reticulate PANI/PSMA composite was, thus, obtained. The adsorption performance of the composite for organic dyes under different circumstances and the adsorption mechanism were studied. The obtained PANI/PSMA composite exhibited a high adsorption rate and adsorption capacity, as well as good adsorption selectivity toward methyl orange (MO). The adsorption process followed pseudo-second-order kinetics and the Langmuir isotherm. The maximum adsorption capacity for MO was 147.93 mg/g. After five cycles of adsorption–desorption, the removal rate remained higher than 90%, which indicated that the adsorbent has great recyclability. The adsorbent materials presented herein would be highly valuable for the removal of organic dyes from wastewater.

The removal of Cr(VI) in wastewater plays an important role in human health and environment. In this work, polypyrrole/hollow mesoporous silica particle (PPy/HMSNs) adsorbents have been newly synthesized by in-situ polymerization, which prevent the aggregation of pyrrole in the process of polymerization and exhibit highly selective and powerful adsorption ability for Cr(VI). The adsorption process was in good agreement with the quasi-second-order kinetic model and the Langmuir isotherm model. And the maximum adsorption capacity of Cr(VI) was 322 mg/g at 25 °C. Moreover, the removal rate of Cr(VI) by PPy/HMSNs was ~100% in a number of binary systems, such as Cl⁻/Cr(VI), NO₃⁻/Cr(VI), SO₄²⁻/Cr(VI), Zn²⁺/Cr(VI), Fe³⁺/Cr(VI), Sn⁴⁺/Cr(VI), and Cu²⁺/Cr(VI). Thus, the PPy/HMSNs adsorbents have great potential for the removal of Cr(VI) in wastewater.