Two-dimensional materials provide extraordinary opportunities for exploring phenomena arising in atomically thin crystals. Beginning with the first isolation of graphene, mechanical exfoliation has been a key to provide high-quality two-dimensional materials, but despite improvements it is still limited in yield, lateral size and contamination. Here we introduce a contamination-free, one-step and universal Au-assisted mechanical exfoliation method and demonstrate its effectiveness by isolating 40 types of single-crystalline monolayers, including elemental two-dimensional crystals, metal-dichalcogenides, magnets and superconductors. Most of them are of millimeter-size and high-quality, as shown by transfer-free measurements of electron microscopy, photo spectroscopies and electrical transport. Large suspended two-dimensional crystals and heterojunctions were also prepared with high-yield. Enhanced adhesion between the crystals and the substrates enables such efficient exfoliation, for which we identify a gold-assisted exfoliation method that underpins a universal route for producing large-area monolayers and thus supports studies of fundamental properties and potential application of two-dimensional materials.

Porous nanotubes comprised of MnO2 nanosheets were fabricated with a one-pot hydrothermal method using polycarbonate membrane as the template. The diameter and thickness of nanotubes can be controlled by choice of the membrane pore size and the chemistry. The porous MnO2 nanotubes were used as a supercapacitor electrode. The specific capacitance in a three-electrode system was 365[emsp14]F g-1 at a current density of 0.25[emsp14]A g-1 with capacitance retention of 90.4% after 3000 cycles. An asymmetric supercapacitor with porous MnO2 nanotubes as the positive electrode and activated graphene as the negative electrode yielded an energy density of 22.5[emsp14]Wh kg-1 and a maximum power density of 146.2[emsp14]kW kg-1; these values exceeded those reported for other MnO2 nanostructures. The supercapacitor performance was correlated with the hierarchical structure of the porous MnO2 nanotubes.