Silicon as a negative electrode material for lithium-ion batteries has attracted tremendous attention due to its high theoretical capacity, and fluoroethylene carbonate (FEC) was used as an electrolyte additive, which significantly improved the cyclability of silicon-based electrodes in this study. The decomposition of the FEC additive was investigated by synchrotron-based X-ray photoelectron spectroscopy (PES) giving a chemical composition depth-profile. The reduction products of FEC were found to mainly consist of LiF and −CHF–OCO₂-type compounds. Moreover, FEC influenced the lithium hexafluorophosphate (LiPF₆) decomposition reaction and may have suppressed further salt degradation. The solid electrolyte interphase (SEI) formed from the decomposition of ethylene carbonate (EC) and diethyl carbonate (DEC), without the FEC additive present, covered surface voids and lead to an increase in polarization. However, in the presence of FEC, which degrades at a higher reduction potential than EC and DEC, instantaneously a conformal SEI was formed on the silicon electrode. This stable SEI layer sufficiently limited the emergence of large cracks and preserved the original surface morphology as well as suppressed the additional SEI formation from the other solvent. This study highlights the vital importance of how the chemical composition and morphology of the SEI influence battery performance.

O1s and S2p XPS spectra of the graphite electrode after the 1 ^st discharge and the schematic representation of the solid electrolyte interface (SEI) layers formed in an SPE-based graphite half-cell.

The microstructural degradation, stabilization, and characterization of layered Ni-rich cathodes for Li-ion batteries are comprehensively reviewed in this paper.