Highly stable silica-coated manganese ferrite nanoparticles were fabricated for application as magnetic resonance imagining (MRI) contrast agents. The manganese ferrite nanoparticles were synthesized using a hydrothermal technique and coated with silica. The particle size was investigated using transmission electron microscopy and was found to be 40–60 nm. The presence of the silica coating on the particle surface was confirmed by Fourier transform infrared spectroscopy. The crystalline structure was investigated by X-ray diffraction, and the particles were revealed to have an inverse spinel structure. Superparamagnetism was confirmed by the magnetic hysteresis curves obtained using a vibrating sample magnetometer. The efficiency of the MRI contrast agents was investigated by using aqueous solutions of the particles in a 4.7 T MRI scanner. The T₁ and T₂ relaxivities of the particles were 1.42 and 60.65 s^-1 mM^-1, respectively, in water. The ratio r₂/r₁ was 48.91, confirming that the silica-coated manganese ferrite nanoparticles were suitable high-efficacy T₂ contrast agents.

The current study explores the prospective of a nitrogen-doped graphene (NG) incorporated into ZnSe-TiO₂ composites via hydrothermal method for supercapacitor electrodes. Structural, morphological, and electronic characterizations are conducted using XRD, SEM, Raman, and UV analyses. The electrochemical study is performed and galvanostatic charge-discharge (GCD) and cyclic voltammetry (CV) are evaluated for the supercapacitor electrode material. Results demonstrate improved performance in the ZnSe-NG-TiO₂ composite, indicating its potential for advanced supercapacitors with enhanced efficiency, stability, and power density. Specific capacity calculations and galvanic charge-discharge experiments confirmed the promising electrochemical activity of ZnSe-NG-TiO₂, which has a specific capacity of 222 C/g. The negative link among specific capacity and current density demonstrated the composite’s potential for high energy density and high-power density electrochemical devices. Overall, the study shows that composite materials derived from multiple families can synergistically improve electrode characteristics for advanced energy storage applications.