Waterborne acrylic coatings, the largest market share of predominant environmentally friendly coatings, face limitations in their extensive application due to their flammability. The flame-retardant properties of the coatings could be significantly enhanced by incorporate inorganic flame retardants. However, inorganic flame retardants tend to aggregate and unevenly disperse in waterborne acrylic coatings, causing a substantial decrease in flame retardancy. In this work, sodium silicate was utilized as a flame retardant, with urea and melamine serving as modifiers and synergistic agents. This combination resulted in the preparation of a sodium silicate/urea/melamine ternary synergistic waterborne acrylic flame-retardant coating. This coating was applied to the surface of poplar veneer to create flame-retardant poplar veneer. Subsequently, various instruments, including a scanning electron microscope (SEM), a limiting oxygen index meter (LOI), a thermogravimetric analyzer (TG), and a cone calorimeter (CONE), were employed to investigate the relevant properties and mechanisms of both the flame-retardant coating and poplar veneer. The results demonstrated that the sodium silicate/urea/melamine ternary synergistic flame retardant did not exhibit aggregation and could be uniformly dispersed in waterborne acrylic coatings. The physical and mechanical properties of the ternary synergistic flame-retardant poplar veneer coating were satisfactory. Melamine and urea, acting as modifiers, not only greatly enhanced the dispersibility of sodium silicate in waterborne acrylic coatings, but also assisted in the formation of a silicon-containing char layer through the generation of nitrogen, achieving ternary synergistic flame retardancy. In conclusion, this work explores a novel method to efficiently and uniformly disperse inorganic flame retardants in organic coatings. It significantly improves the dispersibility and uniformity of inorganic flame retardants in organic polymers, thereby substantially enhancing the flame-retardant performance of coatings. This work provides a theoretical basis for the research and application of new flame-retardant coatings in the field of chemistry and materials.

The incompatibility between inorganic flame retardants and organic acrylic coatings represents a significant challenge that requires resolution. This work selected environmentally friendly organic aqueous acrylic coatings as the substrate, sodium silicate hydrate as the inorganic flame retardant, and melamine cyanurate (MCA) as the flame-retardant modifier and the flame-retardant co-modifier, with the objective of improving the dispersion and flame-retardant properties of sodium silicate hydrate in the aqueous acrylic coatings. Subsequently, the sodium silicate/MCA/waterborne acrylic acid flame-retardant coating was prepared. The flame-retardant treatment was then applied to poplar veneer in order to create a flame-retardant poplar veneer. The dispersion of the flame-retardant coating was characterized by scanning electron microscopy (SEM), energy-dispersive spectroscopy (EDX), and X-ray diffractometry (XRD). Furthermore, the flame-retardant properties of the flame-retardant poplar veneer were analyzed by thermogravimetry (TG), limiting oxygen index (LOI), and cone calorimeter. The results demonstrated that the MCA-modified sodium silicate flame retardant was well dispersed in aqueous acrylic coatings. The results of the flame-retardant properties of the poplar veneer indicated that the ignition time of the 9% flame retardant-treated poplar veneer was increased by 122.7%, the limiting oxygen index value was increased by 43.0%, and the peak heat release rate (pHRR), the peak total heat release rate (pTHR), and the peak mass loss rate were decreased by 19.9%, 10.8%, and 27.2%, respectively, in comparison to the non-flame retardant-treated poplar veneer. Furthermore, the residual char mass increased by 14.4%, and the residual char exhibited enhanced thickness, density, and regularity. The results demonstrated that MCA was an effective promoter of sodium silicate dispersion in acrylic coatings. Furthermore, the sodium silicate/MCA/waterborne acrylic flame-retardant coating significantly enhance the flame retardancy of wood, and its flame retardant mechanism was consistent with the synergistic silicone–nitrogen expansion flame-retardant mechanism. This work presents a novel approach to enhancing the dispersion of inorganic flame retardants in organic coatings, offering a valuable contribution to the advancement of research and application in the domains of innovative flame retardant coatings and flame retardant wood.