Dislocation slips, twinning, shear banding (SBs), strain localization, and martensite formation are a few deformation modes that are activated in BCC metals and alloys. Strain, strain rate, and deformation temperature are other parameters that determine the activation of deformation modes in BCC alloys. This review focuses on several BCC alloys, such as beta-titanium (β-Ti), tantalum (Ta), and ferritic stainless steels (FSSs), all of which exhibit differences in deformation behavior. These alloys often undergo thermo-mechanical processing (TMP) to enhance their mechanical properties. TMP leads to the evolution of deformation-induced products, such as SBs, strain-induced martensite (SIM), strain localizations, and mechanical/deformation twins (DTs) during plastic deformation, while also influencing crystallographic texture. The deformation modes in β-Ti depend upon the stability of the β-phase (i.e., β-stabilizers); low-stability alloys show the formation of SIM along with slips and twins, whereas in highly stable β-Ti alloys, only slip+twin modes are observed as the primary deformation mechanisms. In the case of Ta, slip activity predominantly occurs on {110} planes, but it can also occur on planes with the highest resolved shear stress. The breakdown of Schmid’s law or non-Schmid behavior for Ta and Ta-W alloys has been discussed in detail. The cold rolling (CR) of FSSs results in the formation of ridges, which is an undesirable phenomenon leading to very low formability. The microstructures of the rolled sheets consist of elongated ferrite grains with in-grain SBs, which are preferentially formed in the γ-fiber-oriented grains. The formation of finer grains after recrystallization improves both the mechanical properties and ridging resistance in FSS. Therefore, this review comprehensively reports on the impact of TMP on the microstructural and crystallographic texture evolution during the plastic deformation and annealing treatment of β-Ti, Ta alloys, and FSSs in BCC materials, using results obtained from electron microscopy and X-ray diffraction.

In the present investigation, an attempt has been made to investigate the replacement compatibility of conventional austenitic stainless steel (316L) with low-Ni austenitic stainless steel (201) by employing their dissimilar welding using gas tungsten arc welding technique with varying heat input. The effects of heat input on the microstructural, mechanical, and corrosion properties were studied. The result depicts the balanced austenite/ferrite content in the fusion zone for both the heat inputs. The low heat input process, which results in a faster cooling rate, demonstrates higher tensile strength and microhardness. Similarly, the pitting corrosion resistance of the fusion zone demonstrates better properties on the low heat input process attributed to the lesser dendritic length and lesser interdendritic arm spacing.

The stacking fault energy (SFE) of face-centered cubic (FCC) alloys is a critical parameter that controls microstructural and crystallographic texture evolution during deformation and annealing treatments. This review focuses on several FCC alloys, aluminum (Al), copper (Cu), austenitic stainless steels (ASSs), and high entropy alloys (HEAs), all of which exhibit varying SFEs. These alloys are often subjected to thermo-mechanical processing (TMP) to enhance their mechanical properties. TMP leads to the evolution of deformation-induced products, such as shear bands (SBs), strain-induced martensite (SIM), and mechanical/deformation twins (DTs) during plastic deformation, while also influencing crystallographic texture. High-medium SFE materials, such as Al and Cu, typically exhibit the evolution of Copper-type texture during room temperature rolling (RTR), while low SFE materials, such as ASSs and HEAs, display Brass-type texture at high reduction ratios. Moreover, the presence of second-phase particles/precipitates can also impact the microstructure and texture evolution in Al and Cu alloys. Particle-stimulated nucleation (PSN) during the annealing treatment has been reported for Al, Cu, ASSs, and HEAs, which causes texture weakening. Another interesting observation in severely deformed Cu alloys is the room-temperature softening phenomenon, which is discussed in the reviewed work. Additionally, plastic deformation and heat treatment of ASSs result in phase transformation, which was not observed in Al, Cu, or HEAs. Furthermore, the dependence of special boundaries in HEAs on plastic deformation temperature, strain rate, and annealing temperature is also discussed. Thus, this review comprehensively reports on the impact of TMP on microstructural and crystallographic texture evolution during plastic deformation and the annealing treatment of Al, Cu, ASSs, and HEAs FCC materials, using results obtained from electron microscopy.

In the present study, cold metal transfer arc welding was employed to weld the 304L austenitic stainless steel (ASS) and Ti-stabilized 439 ferritic stainless steel (FSS) using a 309L filler electrode. Dissimilar joints were prepared using low heat input (HI; W1 ~ 247 J/mm) and high HI (W2 ~ 282 J/mm). The solidification mode for both weldments were the ferritic-austenitic mode and the weld zone (WZ) regions of both the weldments consists of columnar austenites, lathy and skeletal ferrite phases. The interfaces between WZ and ASS base metal showed the unmixed zone, whereas a conventional heat-affected zone (HAZ) was formed between the WZ and FSS base metals. The formation of ferrite stringers were observed in the unmixed zone, whereas peppery features of chromium-rich carbides were observed in HAZ. Moreover, electron backscattered diffraction technique was used to distinguish the microstructural differences between W1 and W2 weldments. Increase in the HIs resulted in decreased ferrite fraction in WZ as well as decrease in the mechanical strength of the joints. The W1 weldment depicted higher values of average micro-hardness (WZ ≈ 334.32 HV) than W2 (WZ ≈ 310.92 HV)) weldment. The electrochemical behaviour of the weldments was analysed for both the base metals and WZ of weldments. The higher degree of sensitization (DOS ~ 9.24%) of W1-WZ showed lower intergranular corrosion resistance than W2-WZ (DOS ~ 7.77%), however, the opposite trend was observed for impedance and pitting resistance.