In a previous study, we successfully coated hydroxyapatite (HAp) onto titanium (Ti) plates using the erbium-doped yttrium aluminum garnet pulsed-laser deposition (Er:YAG-PLD) method. In this study, we performed further experiments to validate the in vitro osteogenic properties, macrophage polarization, and in vivo osseointegration activity of HAp-coated Ti (HAp-Ti) plates and screws. Briefly, we coated a HAp film onto the surfaces of Ti plates and screws via Er:YAG-PLD. The surface morphological, elemental, and crystallographic analyses confirmed the successful surface coating. The macrophage polarization and osteogenic induction were evaluated in macrophages and rat bone marrow mesenchymal stem cells, and the in vivo osteogenic properties were studied. The results showed that needle-shaped nano-HAp promoted the early expression of osteogenic and immunogenic genes in the macrophages and induced excellent M2 polarization properties. The calcium deposition and osteocalcin production were significantly higher in the HAp-Ti than in the uncoated Ti. The implantation into rat femurs revealed that the HAp-coated materials had superior osteoinductive and osseointegration activities compared with the Ti, as assessed by microcomputed tomography and histology. Thus, HAp film on sandblasted Ti plates and screws via Er:YAG-PLD enhances hard-tissue differentiation, macrophage polarization, and new bone formation in tissues surrounding implants both in vitro and in vivo.

In recent years, with the advent of a super-aged society, lifelong dental care has gained increasing emphasis, and implant therapy for patients with an edentulous jaw has become a significant option. However, for implant therapy to be suitable for elderly patients with reduced regenerative and immunological capabilities, higher osteoconductive and antimicrobial properties are required on the implant surfaces. Silicon nitride, a non-oxide ceramic known for its excellent mechanical properties and biocompatibility, has demonstrated high potential for inducing hard tissue differentiation and exhibiting antibacterial properties. In this study, silicon nitride was deposited on pure titanium metal surfaces and evaluated for its biocompatibility and antibacterial properties. The findings indicate that silicon nitride improves the hydrophilicity of the material surface, enhancing the initial adhesion of rat bone marrow cells and promoting hard tissue differentiation. Additionally, the antibacterial properties were assessed using Staphylococcus aureus, revealing that the silicon nitride-coated surfaces exhibited significant antibacterial activity. Importantly, no cytotoxicity was observed, suggesting that silicon nitride-coated titanium could serve as a novel implant material.