This research aims to develop fiber-reinforced composites (FRC) with enhanced fire resistance, which can be particularly useful for the transport industry (e.g., aviation, automotive, and train production). The fire retardation was achieved through epoxy matrix modification with hexachlorocyclotriphosphazene (HCTP). First, the fire-resistant and mechanical properties of the epoxy matrix filled with different HCTP contents (4.8, 7.2, and 9.5 wt.%) were studied to select the most effective HCTP content for the impregnation of FRC. Then, glass, basalt, and carbon fiber fabrics were impregnated with epoxy filled with 7.2 wt.% of HCTP, and the fire resistance, flexural, and interlaminar fracture properties were studied to select the most effective HCTP-modified type of fiber reinforcement based on the test results. It was concluded that basalt fiber impregnated with epoxy filled with HCTP could be selected as the most effective reinforcement type, allowing excellent mechanical and flame-retardant properties.

A system of pultruded carbon fibre-reinforced plastics micro-tubes is used for self-healing simulation in laminated polymer composite. The system consists of a package of micro-tubes, placed in the symmetry plane of the GFR/epoxy laminate stack. Healing agent is a mixture of the epoxy resin and hardener. The healing agent releases and penetrates into the cracks after the composite is damaged by the quasi-static indentation. The specimens are healed at 30℃ for 24 h. Rectangular specimens notched under ASTM D2733 have been subjected to tensile test to determine interlaminar shear strength. Shear strength of specimens has been compared in three states (virgin, damaged and healed) for various ways of healing. After the most effective self-healing, the interlaminar shear strength has been recovered to 70 ± 15% of those for virgin specimens that almost twice exceeds the residual strength of the damaged specimens.

A simple and prompt method to determine the mechanical properties of industrial multilayer extrusion polypropylene pipes for a gravity sewer network is suggested. The engineering formulas included for calculating the permissible thickness and relative position of a foam core in the pipes are based on a linear-elastic approximation and the rule of mixtures. The applicability of the approximation was justified experimentally during investigation of the effective tensile characteristics of single- and multilayer pipes and each layer specimen by using traditional tests and finite-element calculations. The results obtained were used to formulate engineering recommendations for calculations of this type.

The spectrometric characteristics of CdZnTe detectors are largely determined by the nonuniformity of the material and the influence of the negative polarization effects associated with the formation of space charges in the sensitive volume of the detector. They change the electric field distribution in the detector and affect the efficiency of the charge carrier collection. An analysis of the waveforms of the output pulses was used to investigate the uniformity of the charge collection and electric field distribution in the detectors when irradiated by the alpha particles. The influence of infrared (IR) illumination on these parameters was evaluated. IR illumination had no positive effect on the planar detector but greatly improved the charge collection in quasi-hemispherical detectors in the peripheral (corner) regions. The output pulse amplitude increased, and the rise time notably decreased. Polarization that occurred predominantly in the corner regions at low temperatures (from −30 °C to −20 °C) was eliminated using IR illumination.