This paper investigates the influence of reaction medium pH on silica-coating of magnetite nanoparticles. Magnetite nanoparticles were prepared by means of a reduction-precipitation method using ferric chloride as a starting material, which was partially reduced to ferrous salts by Na2SO3 before alkalinizing with ammonia. The particles were coated by sol-gel method with either ammonia or HCl aqueous solutions for either base- or acid-catalyzed hydrolysis, respectively. Powder X-ray diffraction, Fourier-transform infrared, and Zeta Potential were used for the characterization of oxides and of the coated magnetic nanoparticles. The observed difference of pH IEP in KCl solution for pure silica (2.0), magnetite (5.0), and silica-coated magnetite (2.3) samples confirms that the coating process was effective since the charge surface properties of coated magnetic nanoparticles are close to that of pure silica, even though the Fourier-transform infrared spectra did not evidence the formation of Fe-O-Si bonds.

This work aimed at putting in evidence the influence of the pH on the chemical nature and properties of the synthesized magnetic nanocomposites. Saturation magnetization measurements evidenced a marked difference of the magnetic behavior of samples, depending on the final pH of the solution after reaction. Magnetite and maghemite in different proportions were the main magnetic iron oxides actually identified. Synthesis with final pH between 9.7-10.6 produced nearly pure magnetite with little or no other associated iron oxide. Under other synthetic conditions, goethite also appears in proportions that depended upon the pH of the synthesis medium.