The CO₂-assisted oxidative dehydrogenation of propane (ODP) was investigated over titania based composite metal oxides, 10% M_xO_y-TiO₂ (M: Zr, Ce, Ca, Cr, Ga). It was found that the surface basicity of composite metal oxides was significantly higher than that of bare TiO₂ and varied in a manner which depended strongly on the nature of the M_xO_y modifier. The addition of metal oxides on the TiO₂ surface resulted in a significant improvement of catalytic performance induced by a synergetic interaction between M_xO_y and TiO₂ support. Propane conversion and propylene yield were strongly influenced by the nature of the metal oxide additive and were found to be superior for the Cr₂O₃-TiO₂ and Ga₂O₃-TiO₂ catalysts characterized by moderate basicity. The reducibility of the latter catalysts was significantly increased, contributing to the improved catalytic performance. This was also the case for the surface acidity of Ga₂O₃-TiO₂ which was found to be higher compared with Cr₂O₃-TiO₂ and TiO₂. A general trend was observed whereby catalytic performance increased significantly with decreasing the primary crystallite size of TiO₂. DRIFTS studies conducted under reaction conditions showed that the adsorption/activation of CO₂ was favored on the surface of composite metal oxides. This may be induced by the improved surface basicity observed with the M_xO_y addition on the TiO₂ surface. The Ga₂O₃ containing sample exhibited sufficient stability for about 30 h on stream, indicating that it is suitable for the production of propylene through ODP with CO₂ reaction.

The oxidative dehydrogenation of propane with CO₂ (CO₂-ODP) was investigated over different metal oxides M_xO_y (M: Ca, Sn, Cr, Ga) supported on a SiO₂ surface. Catalysts were characterized employing nitrogen adsorption/desorption, X-ray diffraction (XRD), CO₂ temperature programmed desorption (CO₂-TPD) and pyridine adsorption/desorption experiments in order to identify their physicochemical properties and correlate them with their activity and selectivity for the CO₂-ODP reaction. The effect of operating reaction conditions on catalytic performance was also examined, aiming to improve the propylene yield and suppress side reactions. Surface acidity and basicity were found to be affected by the nature of M_xO_y, which in turn affected the conversion of propane to propylene, which was in all cases higher compared to that of bare SiO₂. Propane conversion, reaction rate and selectivities towards propylene and carbon monoxide were maximized for the Ga- and Cr-containing catalysts characterized by moderate surface basicity, which were also able to limit the undesired reactions leading to ethylene and methane byproducts. High surface acidity was found to be beneficial for the CO₂-ODP reaction, which, however, should not be excessive to ensure high catalytic activity. The silica-supported Ga₂O₃ catalyst exhibited sufficient stability with time and better than that of the most active Cr₂O₃-SiO₂ catalyst. Decreasing the weight gas hourly space velocity resulted in a significant improvement in both propane conversion and propylene yield as well as a suppression of undesired product formation. Increasing CO₂ concentration in the feed did not practically affect propane conversion, while led to a decrease in propylene yield. The ratio of propylene to ethylene selectivity was optimized for CO₂:C₃H₈ = 5:1 and space velocity of 6000 mL g^?1 h^?1, most possibly due to facilitation of the C–H bond cleavage against that of the C–C bond. Results of the present study provided evidence that the efficient conversion of propane to propylene is feasible over silica-based composite metal oxides, provided that catalyst characteristics have been optimized and reaction conditions have been properly selected.

Propylene production through the CO₂-assisted oxidative dehydrogenation of propane (CO₂-ODP) is an effective route able to address the ever-increasing demand for propylene and simultaneously utilize CO₂. In this study, a series of alumina-supported gallium oxide catalysts of variable Ga₂O₃ loading was synthesized, characterized, and evaluated with respect to their activity for the CO₂-ODP reaction. It was found that both the catalysts’ physicochemical characteristics and performance were strongly affected by the amount of Ga₂O₃ dispersed on Al₂O₃. Surface basicity was maximized for the sample containing 20 wt.% Ga₂O₃, whereas surface acidity was monotonically increased with increasing Ga₂O₃ loading. A volcano-type correlation was found between catalytic performance and acid/base properties, according to which propane conversion and propylene yield exhibited optimum values for intermediate surface basicity and acidity, which both correspond to the sample containing 30 wt.% Ga₂O₃. The dispersion of a suitable amount of Ga₂O₃ on the Al₂O₃ surface not only enhances the conversion of propane to propylene but also suppresses the formation of side products (C₂H₄, CH₄, and C₂H₆) at temperatures of practical interest. The 30%Ga₂O₃-Al₂O₃ catalyst exhibited very good stability at 550 °C, where byproduct formation and carbon deposition were limited. Mechanistic studies indicated that the reaction proceeds through a two-step oxidative route with the participation of CO₂ in the abstraction of H₂, originating from propane dehydrogenation, through the reverse water–gas reaction (RWGS) reaction, shifting the thermodynamic equilibrium towards propylene generation.