Grain-oriented electrical steel (GOES) has been used for many years for application in transformed cores due to its excellent magnetic properties. Magnetic properties are strongly influenced by obtaining a texture with a certain orientation (110) [001] for BCC structure. This is related to the easy direction of magnetization [001]. So far, the main research has been focused on obtaining a strong texture in the last stages of the process. The aim of the present study was to additionally trace textural changes for a slab after the continuous casting (CC) process and for a sheet after the hot rolling process. The scope of such an analysis has not been conducted before. With regard to the state after continuous casting (CC), the texture was related to measurements of the anisotropy of Barkhausen magnetic noises and the macrostructure of the slab. Based on the X-ray diffraction examinations that compared the texture intensity calculated from the texture coefficient of the slab, the hot rolled steel and the final product of grain-oriented electrical steel contained 3.1% of Si. The studies performed with the material taken from three different production steps showed high differences in the values of textural intensity indicating the occurrence of a crystallization texture, especially in the area of the columnar crystal zone; textural weakness after the hot rolling process and high texturing in the final product for textural components corresponding to the desired Goss texture.

Improvement of magnetic properties of electrical steel can be achieved by reduction the size of magnetic domains. The application of local stresses through laser scribing leads to reduced core losses. In order to determine the effect of laser refinement conditions of magnetic domains on the properties of the soft magnetic material, four samples with a thickness 0.23 mm were refined. The refinement of each sample was carried out using different line energies of the laser beam. Estimation of the magnetic domain size was performed using the Jeffries method, the magnetic viewer was used to reveal the domain structure. The measurement of the magnetic properties was performed at a frequency of 50 Hz and an induction of 1.5 T. The analyzed results presented in this work indicate impact of laser refining on magnetic properties of grain oriented electrical steel depending on used laser beam energy.

This paper presents an analysis of non-metallic inclusions occurring in high-silicon steels containing about 3% Si of terms of their type, volume fraction and morphology. The inclusions were divided into 3 main groups: oxides, sulfides, nitrides which together can also form complex. The work was based on numerous metallographic observations in two sections (longitudinal and transverse to the rolling direction). The study was performed on three casts differing in chemical composition. The analyzed casts were characterized by a different content of non-metallic inclusions, which can be associated with slight differences in chemical composition. The analyzed results showed that the most common inclusions were oxides and nitrides. Sulfides occurred sporadically.