The performance and durability of high-pressure fuel systems in combustion engines are critical for consistent operation under extreme conditions. High-pressure fuel systems are traditionally lubricated with fuel that is compressed and delivered to the combustion chamber. However, lubrication with fuel presents significant challenges in these systems when used with low-viscosity fuels, leading to increased wear rates, especially in reciprocating contacts. This study delved into the tribological performance of steels of varying alloy content (annealed and hardened variants of AISI-52100, CF2, and D2) against alumina and hard 52100 counterbody materials in ethanol and decane environments. Friction and wear behaviors were evaluated, highlighting the influence of material interactions and environmental factors. Elastohydrodynamic lubrication analysis of the tested systems indicated that ethanol and decane form lubricating films of nanometer-scale thickness, confirming the boundary lubrication regimes of the performed tests. In summary, the tribological behavior trends were similar for alumina and 52100 counterbodies. Even though soft 52100 steel demonstrated low friction, its wear was the largest for both tested environments and counterface materials. Among all the tested materials, hard D2 experienced the lowest wear. 52100 and D2 steels showed opposite friction change behavior when comparing hard and soft samples, with lower friction observed for softer 52100 steel and harder D2 steel. Meanwhile, the wear was lower for harder candidates than for softer ones independent of the environment and counterbody material. Raman spectroscopy analysis of the formed wear tracks indicated the formation of carbon films with larger intensities of characteristic carbon peaks observed for more wear-resistant materials. These results suggest the synergistic effect of hardness and tribochemical activity in reducing the wear of materials.

Protective coatings are important for enhancing tribological behavior, preventing surface degradation, and reducing friction-induced energy losses during the operation of mechanical systems. Recently, tribocatalytically driven formation of protective carbon films at the contact interface has been demonstrated as a viable approach for repairing and extending the lifetime of protective coatings. Here, we study the effect of catalytic metals, specifically their composition and amount, on the tribocatalysis process. To achieve this, we test the tribological performance of electro-deposited amorphous CoNiP and CoCuP coatings in different hydrocarbon-rich environments. Our results indicate that the tribocatalytic repair of wear-induced damage is optimal when Ni and Cu are included in the Co-P matrix at 5 wt% Ni and 7 wt% Cu, respectively. Characterization of the wear tracks suggests that among the considered samples, the tribofilms formed on the surface of Co7CuP have the highest concentration of graphitic carbon, leading to a more significant reduction in the COF and wear rate. The carbon tribofilm formation was more pronounced in decane and synthetic oil than in ethanol, which is attributed to the difference in the length of the hydrocarbon molecules affecting viscosity and the lubricant film thickness during boundary lubrication sliding.

To enhance the durability and reliability of high-pressure fuel system components operating with low-viscosity fuels, an analysis of the tribological performance of potential coating material candidates was conducted. This study focuses on evaluating the friction and wear characteristics of various coatings widely used by industry for surface protection, including carbides, nitrides, diamond-like carbon (DLC), and solid lubricants, under accelerated reciprocating ball on flat conditions intended to provide information on longer-term operation in fuel pumps. The tribological performance of these coatings in fuels of varying chemistry and viscosity, including ethanol, decane, dodecane, and aviation fuel (F-24), was compared to the mechanical properties of materials, such as hardness and elastic modulus. Results indicate that carbides show the lowest friction and wear values across different fuel environments. CrN-based coatings demonstrate a decrease in friction and wear in comparison to other nitrides. This comprehensive investigation lays the groundwork for informed design decisions in developing high-performance coatings tailored to withstand the challenges of low-viscosity fuel environments.