This study aimed to analyze the printability of corn-based dough during screw-based three-dimensional (3D) food printing (3DFP) by relating its rheological and mechanical properties to its screw-based 3DFP performance, with the objective of providing insights into the utilization of corn-based dough to produce 3D-printed foods. Screw-based 3DFP was performed using seven corn-based doughs with different nixtamalized corn flour (NCF) and water contents. Afterward, their rheological and mechanical properties were analyzed and associated with their screw-based 3DFP performance. The results showed that stable printability was obtained within a specific range of NCF content in the dough (30–32.5 wt%). Below this range, the 3D-printed foods flattened, while above it, the extrudability of the dough was affected. The printability of the dough was influenced by different rheological and mechanical properties, depending on the stage of the screw-based 3DFP process. During the extrusion stage, the loss tangent at nozzle strain, yield stress, apparent viscosity, and adhesiveness mainly affected the extrudability of the dough. In contrast, the loss tangent at minimum strain, elastic modulus, Young’s modulus, and hardness influenced the self-supporting stage. Therefore, it is important to find a balance between all of these properties, where stable extrudability and self-supporting of the 3D structure are achieved.

Extrusion-based three-dimensional (3D) food printing (3DFP) enhances the customization of 3D-printed foods by using multiple food pastes. Post-printing processes like baking are usually necessary and significantly impact the stability of the 3D-printed foods. This study aimed to produce multi-material 3D-printed foods using nixtamalized corn dough and chickpea paste (CP) in extrusion-based 3DFP and to study the effect of post-printing processes (water oven cooking and steam cooking) and the type of material used (single- or multi-material) on the final appearance, weight, size, and texture of the 3D-printed foods. Multi-material 3D-printed foods were successfully produced using extrusion-based 3DFP. Steam-cooked 3D-printed foods cooked uniformly and had a better appearance, as they did not develop surface cracks compared to water oven-cooked foods. Water-oven cooked foods experienced a greater weight loss of 35.6%, and higher height and length reduction of 1.5% and 8.4%, respectively. Steam-cooked multi-material 3D-printed foods were harder at 40% of strain, with force values of 66.9 and 46.3 N for water-oven cooked foods. Post-printing processes, as well as the presence of CP in the middle of the 3D-printed foods, influenced their final appearance, weight, size, and texture. This study offers interesting findings for the innovative design of chickpea- and corn-based multi-material 3D-printed foods.