The choice of precursor and simple synthesis techniques have decisive roles in the viable production and commercialization of carbon products. The intense demand for developing high-purity carbon nanomaterials through inexpensive techniques has promoted the usage of fossil derivatives as a feasible source of carbon. In this study, Vietnamese-coal-derived porous carbon (PC) was used to fabricate coal-derived porous carbon nanomaterials (CDPCs) using the modified Hummers method. The resulting porous carbon nanomaterials achieved a nanoscale structure with an average pore size ranging from 3 to 10 nm. The findings indicate that CDPC exhibits well-developed micropores and mesopores. The presence of macropores and mesopores not only facilitates the complete immersion of the material in the electrolyte but also effectively shortens the ion diffusion pathways. CDPC boasts a high carbon content, constituting 80.88% by weight. Electrochemical impedance spectroscopy (EIS) Nyquist plot of electrodes made from CDPC showed good conductivity value with low charge-transfer resistance. This electrode worked well and stably with capacitance retention of 74.7% after 1000 cycles. The CDPC specific capacitance reached 236 F/g under a current density of 0.1 A using the constant current discharge method and then decreased as the current density increased. Based on the results of the electrochemical properties of the materials, the energy storage capacity of the CDPC material was good and stable. This investigation presents an eco-friendly methodology for the judicious utilization of coal in energy storage applications, specifically as electrodes for supercapacitors and anodes for Li-ion batteries.