The Fe₃O₄@SiO₂@ZnO composite was synthesized via the simultaneous deposition of SiO₂ and ZnO onto pre-prepared Fe₃O₄ nanoparticles. Physicochemical methods (TEM, EDXS, XRD, SEM, FTIR, PL, zeta potential measurements, and low-temperature nitrogen adsorption/desorption) revealed that the simultaneous deposition onto magnetite surfaces, up to 18 nm in size, results in the formation of an amorphous shell composed of a mixture of zinc and silicon oxides. This composite underwent modification to form Fe₃O₄@SiO₂@ZnO*, achieved by activation with H₂O₂. The modified composite retained its structural integrity, but its surface groups underwent significant changes, exhibiting pronounced catalytic activity in the photodegradation of methyl orange under UV irradiation. It was capable of degrading 96% of this azo dye in 240 min, compared to the initial Fe₃O₄@SiO₂@ZnO composite, which could remove only 11% under identical conditions. Fe₃O₄@SiO₂@ZnO* demonstrated robust stability after three cycles of use in dye photodegradation. Furthermore, Fe₃O₄@SiO₂@ZnO* exhibited decreased PL intensity, indicating an enhanced efficiency in electron-hole pair separation and a reduced recombination rate in the modified composite. The activation process diminishes the electron-hole (e⁻)/(h⁺) recombination and generates the potent oxidizing species, hydroxyl radicals (OH˙), on the photocatalyst surface, thereby playing a crucial role in the enhanced photodegradation efficiency of methyl orange with Fe₃O₄@SiO₂@ZnO*.

Nanostructured nickel exhibits substantial surface area per unit volume and adjustable optical, electronic, magnetic, and biological properties, that makes nanofabricated nickel highly attractive as regards to its practical application in different fields of chemistry. Technologies on nickel nanomaterials including their simple preparation and modern application are summarized in this review.