Passive films formed on stainless steels in a borate buffer solution (pH 9.2) have been investigated by capacitance measurements and photoelectrochemistry. The study was carried out on films formed on AISI type 304 and 316 stainless steels and high purity alloys with differing chromium, nickel, and molybdenum contents. Complementary research by Auger analysis shows that the passive films are composed essentially of an inner chromium region in contact with the metallic substrate and an outer iron oxide region developed at the film/electrolyte interface. The semiconducting properties of the passive films are determined by those of the constituent chromium and iron oxides which are of p‐type and n‐type, respectively. Thus the influence of the alloying elements on the semiconducting properties of the passive films is explained by changes in the electronic structure of each of these two oxide regions.

Mott‐Schottky plots and photoelectrochemical measurements were made on films formed at different potentials on AISI 304 stainless steel in a borate/boric acid solution, pH 9.2. The results allowed the determination of the semiconductive properties and band structure of the films, which account for the existence of two kinds of films depending on the formation potential. For potentials below 0 V (SCE), the results point out for a film with an inverse spinel structure constituted by Cr‐substituted magnetite with two donor levels. Above 0 V only one donor level is detected, which should be Fe²⁺on tetrahedral sites.