Large-scale strandings of Sargassum spp. seaweeds occur annually on the beaches of the Caribbean islands and cause major environmental, health, and economic problems. In order to support an approach of valorisation of algae, an exhaustive characterisation of the composition of these seaweeds has been performed by analysing the contents in alginates, structural carbohydrates (fucans and glucans), minerals, proteins, lipids, mannitol, polyphenols, and heavy metals. Nine batches were collected at different harvesting sites over the years 2021 and 2022, to estimate the spatial and temporal variation in Sargassum composition. A batch of floats was harvested and analysed to estimate the differences in composition between floats and whole algae. Samples collected during the same year (floats or entire plant, freshly collected or stored) showed no significant differences in composition. However, slight differences were observed between batches collected in the two years. Some samples showed significant amounts of heavy metals, especially arsenic. A detailed structural carbohydrates analysis was carried out and discussed with literature data. As the nitrogen content of algae is an interesting parameter for food or agronomic uses, protein analysis enabled us to calculate a new nitrogen–protein conversion factor, specific to these algae species.

Since 2010, huge quantities of Sargassum spp. algae have been proliferating in the Atlantic Ocean and stranding on Caribbean beaches, causing major economic, environmental, and health problems. In this study, an innovative high-density binderless particleboard was developed using uniaxial thermo-compression coupled with a cooling system. The raw material consisted of ground Sargassum seaweeds pre-treated by twin-screw extrusion with water to remove sea salt. The raw material and the particleboards were produced by using various analytical techniques such as Dynamic Vapor Sorption (DVS), Differential Scanning Calorimetry (DSC), Dynamic Mechanical Analysis (DMA), or Thermogravimetric Analysis (TGA). The experimental conditions for thermo-compression (temperature, pressure, time) were evaluated. The best thermo-compression conditions tested were 200 °C, 40 MPa pressure for 7.5 min. This resulted in a particleboard with high density (up to 1.63 ± 0.02 g/cm³) and high flexural strength/modulus (up to 32.3 ± 1.8 MPa/6.8 ± 0.2 GPa, respectively), but a low water contact angle of 38.9° ± 3.5°. Thermal analyses revealed the effect of alginates on the mechanical properties of particleboards. This work opens the door to a new way of adding value to Sargassum seaweed, using the whole algae with minimal pre-treatment.

This study aimed to evaluate the effects of mechanical treatment through twin-screw extrusion for the enhancement of biomethane production. Four lignocellulosic biomasses (i.e., sweetcorn by-products, whole triticale, corn stover and wheat straw) were evaluated, and two different shear stress screw profiles were tested. Chemical composition, particle size reduction, tapped density and cellulose crystallinity were assessed to show the effect of extrusion pretreatment on substrate physico-chemical properties and their biochemical methane production (BMP) capacities. Both mechanical pretreatments allowed an increase in the proportion of particles with a diameter size less than 1 mm (from 3.7% to 72.7%). The most restrictive profile also allowed a significant solubilization of water soluble coumpounds, from 5.5% to 13%. This high-shear extrusion also revealed a reduction in cellulose crystallinity for corn stover (i.e., 8.6% reduction). Sweetcorn by-products revealed the highest BMP values (338–345 NmL/gVS), followed by corn stover (264–286 NmL/gVS), wheat straw (247–270 NmL/gVS) and whole triticale (233–247 NmL/gVS). However, no statistical improvement in maximal BMP production was provided by twin-screw extrusion. Nevertheless, BMP kinetic analysis proved that both extrusion pretreatments were able to increase the specific rate constant (from 13% to 56% for soft extrusion and from 66% to 107% for the high-shear one).