The effect of aging treatments at various temperatures on the mechanical properties and microstructure of 10B21 cold heading steel with a 20% reduction in area (ε = 0.1) was investigated. The mechanical properties were evaluated based on tensile tests and hardness tests, while the evolution of microstructure was observed by using an optical microscope (OM), scanning electron microscope (SEM), transmission electron microscope (TEM) and X-ray diffraction (XRD). The results reveal that aging treatment enhance the strength and hardness of 10B21 cold heading steel after drawing, and the highest values of strength and hardness are attained at an aging temperature of 300 °C. Specifically, the yield and ultrahigh tensile strength after aging at 300 °C are measured at 620 MPa and 685 MPa, respectively, which are 30 MPa and 50 MPa higher than the cold-drawn sample. Moreover, the hardness after aging at 300 °C reaches 293 HV, which has an increase of 30 HV compared to the cold-drawn state. The improvement in mechanical properties may be related to the strain-aging mechanism and the increased density of dislocations. In addition, the analysis of the TEM results reveal that the presence of the second-phase Ti(C,N) contributes to pinning the dislocations, whereas the dislocations are pinned between the cementite (Fe₃C) lamellar and stacked at the grain boundaries, leading to strain hardening of the material.

The CASTRIP process is an innovative method for producing flat rolled low-carbon and low-alloy steel at very thin thicknesses. By casting steel close to its final dimensions, enormous savings in time and energy can be realized. In this paper, an ultra-high-strength low-alloy corrosion-resistant steel was produced through the CASTRIP process. Microstructure and properties were investigated by means of optical microscopy (OM), scanning electron microscopy (SEM), transmission electron microscopy (TEM), laser confocal microscopy (LSCM), electron backscattered diffraction (EBSD), and tensile testing. The results show that the microstructure is mainly composed of polygonal ferrite, bainite ferrite, and acicular ferrite. The bainite ferrite forms parallel lath bundles nucleating at austenite grain boundaries, propagating perpendicularly into the parent grains. The acicular ferrite exhibits a cross-interlocked morphology preferentially nucleating at oxide/sulfide inclusions. Microstructural characterization confirms that the phase transformation of acicular ferrite and bainite ferrite introduces high-density dislocations, identified as the primary strengthening mechanism. Under the CASTRIP process, corrosion-resistant elements such as Cu, P, Sb, and Nb are completely dissolved in the matrix without grain boundary segregation, thereby contributing to solid solution strengthening.