InP quantum dots (QDs) are considered as the most promising alternative to Cd-based QDs with lower toxicity, and emission spectrum tunability ranging from the visible to near-infrared region. Although high-quality fluorescent InP QDs have been successfully synthesized by several groups, the rigorous synthesis conditions hinder its practical use in display devices. In this work, for the first time, we introduce Zn²⁺ into the growth stage of the InP QDs to prepare an InP–In(Zn)P core, and then the as-grown InP–In(Zn)P cores were consecutively coated with typical double shells of inner ZnSe and outer ZnS. The final InP–In(Zn)P/ZnSe/ZnS core/shell/shell QDs exhibited a maximum photoluminescence (PL) quantum yield (QY) of 94.3% and have tunable emissions from yellow (569 nm) to red (630 nm), showing a potential application in display devices. Above all, compared with other related studies, the excellent PL properties were obtained in relatively milder conditions (ultimate vacuum level of 400 mTorr). The results of this study provide guidance for the commercial application of InP QDs as a viable alternative to Cd-based QDs.

Adding corrosion inhibitors is considered to be a cost-effective way to inhibit metal corrosion. In this study, we report the synthesis of a bi-mannich base corrosion inhibitor (BMT) with an impressive inhibition efficiency on carbon steel in H₂S and HCl co-existing solution. At the BMT concentration of 9 ppm, the inhibition efficiency (η) of 96.9%, 97.6% and 98.0% were determined by weight loss, potentiodynamic polarization and electrochemical impedance spectroscopy, respectively. The adsorption of BMT on the carbon steel surface follows the Langmuir adsorption isotherm, and the calculated free energy indicates that the adsorption is a spontaneous process. This research also delves into understanding the adsorption behavior and corrosion inhibition mechanism of BMT on carbon steel surfaces through quantum chemistry calculations. The results of this study provide guidance for the application of BMT as a corrosion inhibitor in sour and acid environments.