Gellan gum microspheres were obtained by ionotropic gelation technique, using the trivalent ion Al³⁺. The percentage of entrapment efficiency ranged from 48.76 to 87.52% and 2² randomized full factorial design demonstrated that both the increase of polymer concentration and the decrease of crosslinker concentration presented a positive effect in the amount of encapsulated drug. Microspheres size and circularity ranged from 700.17 to 938.32 μm and from 0.641 to 0.796 μm, respectively. The increase of polymer concentration (1–2%) and crosslinker concentration (3–5%) led to the enlargement of particle size and circularity. However, the association of increased crosslinker concentration and reduced polymer content made the particles more irregular. In vitro and ex vivo tests evidenced the high mucoadhesiveness of microspheres. The high liquid uptake ability of the microspheres was demonstrated and the pH variation did not affect this parameter. Drug release was pH dependent, with low release rates in acid pH (42.40% and 44.93%) and a burst effect in phosphate buffer pH (7.4). The Weibull model had the best correlation with the drug release data, demonstrating that the release process was driven by a complex mechanism involving the erosion and swelling of the matrix or by non-Fickian diffusion.

This work addresses the establishment and characterization of gellan gum:pectin (GG:P) biodegradable mucoadhesive beads intended for the colon-targeted delivery of resveratrol (RES). The impact of the polymer carrier system on the cytotoxicity and permeability of RES was evaluated. Beads of circular shape (circularity index of 0.81) with an average diameter of 914 μm, Span index of 0.29, and RES entrapment efficiency of 76% were developed. In vitro drug release demonstrated that beads were able to reduce release rates in gastric media and control release for up to 48 h at an intestinal pH of 6.8. Weibull’s model correlated better with release data and b parameter (0.79) indicated that the release process was driven by a combination of Fickian diffusion and Case II transport, indicating that both diffusion and swelling/polymer chains relaxation are processes that contribute equally to control drug release rates. Beads and isolated polymers were observed to be safe for Caco-2 and HT29-MTX intestinal cell lines. RES encapsulation into the beads allowed for an expressive reduction of drug permeation in an in vitro triple intestinal model. This feature, associated with low RES release rates in acidic media, can favor targeted drug delivery from the beads in the colon, a promising behavior to improve the local activity of RES.

Nanoparticles based on gellan gum/pectin blends were designed for colon-targeted release of resveratrol (RES). Their impact on drug release rates and permeability were evaluated using Caco-2 cell model and mucus secreting triple co-culture model. Polymeric nanoparticles (PNP) were successfully prepared by nebulization/ionotropic gelation, achieving high drug loading (>80%). PNP were spherical with a low positive charge density (+5mV) and exhibited diameters of around 330nm. Developed PNP were able to promote effective modulation of drug release rates, so that only 3% of RES was released in acidic media over 2 hours, and, in pH 6.8, the drug was released in a sustained manner, reaching 85% in 30 hours. The permeability of RES-loaded PNP in the Caco-2 model was 0.15%, while in the triple co-culture model, in the presence of mucus, it reached 5.5%. The everted gut sac experiment corroborated the low permeability of RES-loaded PNP in the presence or absence of mucus and highlighted their high ability to interact with the intestinal tissue. Results indicate that the novel PNP developed in this work are safe and promising carriers for controlled delivery of RES at the colon.

Films of gellan gum:pectin blends were prepared by solvent casting method. Gellan gum:pectin mass ratios were varied (4:1; 1:1; 1:4) at different concentrations (3% or 4%) and glycerol was used as plasticizer (1 or 2%). The films were thin (18 to 30 µm), translucent, flexible, and homogeneous. The surface pH was suitable for buccal application. All films reached high mechanical resistance and the mucoadhesive ability of them was evidenced. High ratio of gellan gum improved the mechanical resistance and the mucoadhesion of the films as well as the control of drug release rates. The films did not disintegrate in simulate saliva up to 24 hours and curcumin release could be sustained up to 12 hours. The set of data evidence that the films designed in this work represent a potential platform for buccal drug delivery.